Nickel Alloy 890 (N08890)

Nickel Alloys

Overview Chemical Composition Mechanical Properties Physical Properties Other Properties

Property Overview

Density8.1g/cm³

Elastic Modulus200GPa

Tensile Strength590MPa

Yield Strength230MPa

Brinell HardnessUnknown

Maximum Service Temperature1000°C

Weight Calculator

Chemical Composition

0.060 to 0.14%

23.5 to 28.5%

40 to 45%

1.0 to 2.0%

0 to 1.5%

1.0 to 2.0%

0 to 0.015%

0 to 0.75%

0.2 to 1.0%

0.15 to 0.6%

0.050 to 0.6%

0.1 to 0.6%

17.3 to 33.9%

Mechanical

Elastic (Young's, Tensile) Modulus

200 GPa

Elongation at Break

39 %

Fatigue Strength

180 MPa

Poisson's Ratio

0.28

Shear Modulus

78 GPa

Shear Strength

400 MPa

Tensile Strength: Ultimate (UTS)

590 MPa

Tensile Strength: Yield (Proof)

230 MPa

Physical

Density

8.1 g/cm 3

Thermal

Latent Heat of Fusion

330 J/g

Maximum Temperature: Mechanical

1000 °C

Melting Completion (Liquidus)

1390 °C

Melting Onset (Solidus)

1340 °C

Specific Heat Capacity

480 J/kg-K

Thermal Expansion

14 µm/m-K

Thermal Shock Resistance

15 points

Calculated

Resilience: Ultimate (Unit Rupture Work)

180 MJ/m 3

Resilience: Unit (Modulus of Resilience)

140 kJ/m 3

Stiffness to Weight: Axial

14 points

Stiffness to Weight: Bending

24 points

Strength to Weight: Axial

20 points

Strength to Weight: Bending

19 points

Environmental

Base Metal Price

47 % relative

Embodied Carbon

8.2 kg CO 2 /kg material

Embodied Energy

120 MJ/kg

Embodied Energy

120 MJ/kg 52 x 10 3 BTU/lb

Embodied Water

250 L/kg

Embodied Water

250 L/kg 30 gal/lb

Registered Designations & Aliases

N08890Nickel Alloy 890 (N08890)

Standards

ASTM B407 ASTM B407: Standard Specification for Nickel-Iron-Chromium Alloy Seamless Pipe and Tube

ASTM B408 ASTM B408: Standard Specification for Nickel-Iron-Chromium Alloy Rod and Bar

ASTM B408 ASTM B408: Standard Specification for Nickel-Iron-Chromium Alloy Rod and Bar ASTM B409: Standard Specification for Nickel-Iron-Chromium Alloy Plate, Sheet, and Strip ASTM B407: Standard Specification for Nickel-Iron-Chromium Alloy Seamless Pipe and Tube Microstructure of Superalloys, Madeleine Durand-Charre, 1998 Aerospace Materials, Brian Cantor et al. (editors), 2001 Engineering Properties of Nickel and Nickel Alloys, John L. Everhart, 1971 Nickel Alloys, Ulrich Heubner (editor), 1998

ASTM B409 ASTM B409: Standard Specification for Nickel-Iron-Chromium Alloy Plate, Sheet, and Strip