فا

Nickel Alloy 600 (N06600, NA14)

Nickel Alloys

annealed
OverviewChemical CompositionMechanical PropertiesPhysical PropertiesOther Properties

Property Overview

Density8.5g/cm³
Elastic Modulus190GPa
Tensile Strength650MPa
Yield Strength280MPa
Brinell HardnessUnknown
Maximum Service Temperature1100°C
Weight Calculator

Chemical Composition

C
0 to 0.15%
CR
14 to 17%
NI
72 to 80%
MN
0 to 1.0%
SI
0 to 0.5%
S
0 to 0.015%
CU
0 to 0.5%
FE
6.0 to 10%

Mechanical

Elastic (Young's, Tensile) Modulus
190 GPa
Elongation at Break
35 %
Fatigue Strength
270 MPa
Poisson's Ratio
0.29
Shear Modulus
75 GPa
Shear Strength
440 MPa
Tensile Strength: Ultimate (UTS)
650 MPa
Tensile Strength: Yield (Proof)
280 MPa

Physical

Density
8.5 g/cm 3

Thermal

Curie Temperature
-120 °C
Latent Heat of Fusion
310 J/g
Maximum Temperature: Mechanical
1100 °C
Melting Completion (Liquidus)
1410 °C
Melting Onset (Solidus)
1350 °C
Specific Heat Capacity
460 J/kg-K
Thermal Conductivity
14 W/m-K
Thermal Diffusivity
3.6 mm 2 /s
Thermal Expansion
13 µm/m-K
Thermal Shock Resistance
19 points

Electrical

Electrical Conductivity: Equal Volume
1.7 % IACS
Electrical Conductivity: Equal Weight (Specific)
1.8 % IACS

Calculated

Resilience: Ultimate (Unit Rupture Work)
180 MJ/m 3
Resilience: Unit (Modulus of Resilience)
200 kJ/m 3
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
23 points
Strength to Weight: Axial
21 points
Strength to Weight: Bending
20 points

Environmental

Base Metal Price
55 % relative
Embodied Carbon
9.0 kg CO 2 /kg material
Embodied Energy
130 MJ/kg
Embodied Energy
130 MJ/kg 54 x 10 3 BTU/lb
Embodied Water
250 L/kg
Embodied Water
250 L/kg 30 gal/lb

Physical Other

Calomel Potential
-170 mV
Registered Designations & Aliases
N06600NA14Nickel Alloy 600 (N06600, NA14)
Standards

ASTM B166 ASTM B166: Standard Specification for Nickel-Chromium-Iron Alloys (UNS N06600, N06601, N06603, N06690, N06693, N06025, and N06045) and Nickel-Chromium-Cobalt-Molybdenum Alloy (UNS N06617) Rod, Bar, and Wire

ASTM B167 ASTM B167: Standard Specification for Nickel-Chromium-Iron Alloys (UNS N06600, N06601, N06603, N06690, N06693, N06025, and N06045) and Nickel-Chromium-Cobalt-Molybdenum Alloy (UNS N06617) Seamless Pipe and Tube

ASTM B168 ASTM B168: Standard Specification Nickel-Chromium-Iron Alloys (UNS N06600, N06601, N06603, N06690, N06693, N06025, and N06045) and Nickel-Chromium-Cobalt-Molybdenum Alloy (UNS N06617) Plate, Sheet, and Strip

ASTM B516 ASTM B516: Standard Specification for Welded Nickel-Chromium-Iron Alloy (UNS N06600, UNS N06603, UNS N06025, and UNS N06045) Tubes

ASTM B516 ASTM B516: Standard Specification for Welded Nickel-Chromium-Iron Alloy (UNS N06600, UNS N06603, UNS N06025, and UNS N06045) Tubes ASTM B517: Standard Specification for Welded Nickel-Chromium-Iron-Alloy (UNS N06600, UNS N06603, UNS N06025, and UNS N06045) Pipe ASTM B166: Standard Specification for Nickel-Chromium-Iron Alloys (UNS N06600, N06601, N06603, N06690, N06693, N06025, and N06045) and Nickel-Chromium-Cobalt-Molybdenum Alloy (UNS N06617) Rod, Bar, and Wire ASTM B167: Standard Specification for Nickel-Chromium-Iron Alloys (UNS N06600, N06601, N06603, N06690, N06693, N06025, and N06045) and Nickel-Chromium-Cobalt-Molybdenum Alloy (UNS N06617) Seamless Pipe and Tube ASTM B168: Standard Specification Nickel-Chromium-Iron Alloys (UNS N06600, N06601, N06603, N06690, N06693, N06025, and N06045) and Nickel-Chromium-Cobalt-Molybdenum Alloy (UNS N06617) Plate, Sheet, and Strip ASTM B564: Standard Specification for Nickel Alloy Forgings Microstructure of Superalloys, Madeleine Durand-Charre, 1998

ASTM B517 ASTM B517: Standard Specification for Welded Nickel-Chromium-Iron-Alloy (UNS N06600, UNS N06603, UNS N06025, and UNS N06045) Pipe

ASTM B564 ASTM B564: Standard Specification for Nickel Alloy Forgings