Nickel Alloy 333 (N06333)

Nickel Alloys

Overview Chemical Composition Mechanical Properties Physical Properties Other Properties

Property Overview

Density8.5g/cm³

Elastic Modulus210GPa

Tensile Strength630MPa

Yield Strength270MPa

Brinell HardnessUnknown

Maximum Service Temperature1010°C

Weight Calculator

Chemical Composition

0 to 0.1%

24 to 27%

44 to 48%

2.5 to 4.0%

0 to 2.0%

0 to 1.5%

0 to 0.030%

2.5 to 4.0%

9.3 to 24.5%

Mechanical

Elastic (Young's, Tensile) Modulus

210 GPa

Elongation at Break

34 %

Fatigue Strength

200 MPa

Poisson's Ratio

0.28

Shear Modulus

81 GPa

Shear Strength

420 MPa

Tensile Strength: Ultimate (UTS)

630 MPa

Tensile Strength: Yield (Proof)

270 MPa

Hardness

Rockwell B Hardness

Physical

Density

8.5 g/cm 3

Thermal

Latent Heat of Fusion

320 J/g

Maximum Temperature: Mechanical

1010 °C

Melting Completion (Liquidus)

1460 °C

Melting Onset (Solidus)

1410 °C

Specific Heat Capacity

450 J/kg-K

Thermal Conductivity

11 W/m-K

Thermal Diffusivity

2.9 mm 2 /s

Thermal Expansion

13 µm/m-K

Thermal Shock Resistance

16 points

Electrical

Electrical Conductivity: Equal Volume

1.5 % IACS

Electrical Conductivity: Equal Weight (Specific)

1.6 % IACS

Calculated

Resilience: Ultimate (Unit Rupture Work)

170 MJ/m 3

Resilience: Unit (Modulus of Resilience)

180 kJ/m 3

Stiffness to Weight: Axial

14 points

Stiffness to Weight: Bending

23 points

Strength to Weight: Axial

21 points

Strength to Weight: Bending

19 points

Environmental

Base Metal Price

55 % relative

Embodied Carbon

8.5 kg CO 2 /kg material

Embodied Energy

120 MJ/kg

Embodied Energy

120 MJ/kg 51 x 10 3 BTU/lb

Embodied Water

270 L/kg

Embodied Water

270 L/kg 33 gal/lb

Registered Designations & Aliases

N06333Nickel Alloy 333 (N06333)

Standards

ASTM B718 ASTM B718: Standard Specification for Nickel-Chromium-Molybdenum-Cobalt-Tungsten-Iron-Silicon Alloy (UNS N06333) Plate, Sheet, and Strip

ASTM B718 ASTM B718: Standard Specification for Nickel-Chromium-Molybdenum-Cobalt-Tungsten-Iron-Silicon Alloy (UNS N06333) Plate, Sheet, and Strip ASTM B719: Standard Specification for Nickel-Chromium-Molybdenum-Cobalt-Tungsten- Iron-Silicon Alloy (UNS N06333) Bar ASTM B722: Standard Specification for Nickel-Chromium-Molybdenum-Cobalt-Tungsten-Iron-Silicon Alloy (UNS N06333) Seamless Pipe and Tube ASTM B723: Standard Specification for Nickel-Chromium-Molybdenum-Cobalt-Tungsten-Iron-Silicon Alloy (UNS N06333) Welded Pipe ASTM B726: Standard Specification for Nickel-Chromium-Molybdenum-Cobalt-Tungsten-Iron-Silicon Alloy (UNS N06333) Welded Tube Engineering Properties of Nickel and Nickel Alloys, John L. Everhart, 1971 Nickel Alloys, Ulrich Heubner (editor), 1998

ASTM B719 ASTM B719: Standard Specification for Nickel-Chromium-Molybdenum-Cobalt-Tungsten- Iron-Silicon Alloy (UNS N06333) Bar

ASTM B722 ASTM B722: Standard Specification for Nickel-Chromium-Molybdenum-Cobalt-Tungsten-Iron-Silicon Alloy (UNS N06333) Seamless Pipe and Tube

ASTM B723 ASTM B723: Standard Specification for Nickel-Chromium-Molybdenum-Cobalt-Tungsten-Iron-Silicon Alloy (UNS N06333) Welded Pipe

ASTM B726 ASTM B726: Standard Specification for Nickel-Chromium-Molybdenum-Cobalt-Tungsten-Iron-Silicon Alloy (UNS N06333) Welded Tube