AWS ERNiMo-3 Weld Metal
Nickel Welding & Filler Materials
Property Overview
Density9.1g/cm³
Elastic Modulus220GPa
Tensile Strength770MPa
Yield StrengthUnknown
Brinell HardnessUnknown
Maximum Service TemperatureUnknown
Chemical Composition
C
0 to 0.12%
CR
4.0 to 6.0%
NI
53.7 to 69%
MO
23 to 26%
MN
0 to 1.0%
SI
0 to 1.0%
P
0 to 0.040%
S
0 to 0.030%
CU
0 to 0.5%
V
0 to 0.6%
CO
0 to 2.5%
W
0 to 1.0%
RES.
Residuals res. | | 0 to 0.5%
RESIDUALS RES.
0 to 0.5%
FE
4.0 to 7.0%
Mechanical
Elastic (Young's, Tensile) Modulus
220 GPa
Poisson's Ratio
0.3
Shear Modulus
83 GPa
Tensile Strength: Ultimate (UTS)
770 MPa
Physical
Density
9.1 g/cm 3
Thermal
Latent Heat of Fusion
320 J/g
Melting Completion (Liquidus)
1600 °C
Melting Onset (Solidus)
1540 °C
Specific Heat Capacity
400 J/kg-K
Thermal Expansion
11 µm/m-K
Thermal Shock Resistance
24 points
Calculated
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
22 points
Strength to Weight: Axial
24 points
Strength to Weight: Bending
21 points
Environmental
Base Metal Price
70 % relative
Embodied Carbon
15 kg CO 2 /kg material
Embodied Energy
190 MJ/kg
Embodied Energy
190 MJ/kg 82 x 10 3 BTU/lb
Embodied Water
270 L/kg
Embodied Water
270 L/kg 32 gal/lb
Registered Designations & Aliases
AWS ERNiMo-3 Weld Metal