AWS ERNiCrMo-2 Weld Metal
Nickel Welding & Filler Materials
Property Overview
Density8.4g/cm³
Elastic Modulus210GPa
Tensile Strength750MPa
Yield StrengthUnknown
Brinell HardnessUnknown
Maximum Service TemperatureUnknown
Chemical Composition
C
0.050 to 0.15%
CR
20.5 to 23%
NI
40.3 to 53.8%
MO
8.0 to 10%
MN
0 to 1.0%
SI
0 to 1.0%
P
0 to 0.040%
S
0 to 0.030%
CU
0 to 0.5%
CO
0.5 to 2.5%
W
0.2 to 1.0%
RES.
Residuals res. | | 0 to 0.5%
RESIDUALS RES.
0 to 0.5%
FE
17 to 20%
Mechanical
Elastic (Young's, Tensile) Modulus
210 GPa
Poisson's Ratio
0.28
Shear Modulus
81 GPa
Tensile Strength: Ultimate (UTS)
750 MPa
Physical
Density
8.4 g/cm 3
Thermal
Latent Heat of Fusion
320 J/g
Melting Completion (Liquidus)
1460 °C
Melting Onset (Solidus)
1410 °C
Specific Heat Capacity
450 J/kg-K
Thermal Conductivity
11 W/m-K
Thermal Diffusivity
2.9 mm 2 /s
Thermal Expansion
13 µm/m-K
Thermal Shock Resistance
20 points
Electrical
Electrical Conductivity: Equal Volume
1.5 % IACS
Electrical Conductivity: Equal Weight (Specific)
1.6 % IACS
Calculated
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
23 points
Strength to Weight: Axial
25 points
Strength to Weight: Bending
22 points
Environmental
Base Metal Price
55 % relative
Embodied Carbon
9.2 kg CO 2 /kg material
Embodied Energy
120 MJ/kg
Embodied Energy
120 MJ/kg 54 x 10 3 BTU/lb
Embodied Water
270 L/kg
Embodied Water
270 L/kg 32 gal/lb
Registered Designations & Aliases
AWS ERNiCrMo-2 Weld Metal