AWS ERNiCrMo-10 Weld Metal
Nickel Welding & Filler Materials
Property Overview
Density8.9g/cm³
Elastic Modulus220GPa
Tensile Strength790MPa
Yield StrengthUnknown
Brinell HardnessUnknown
Maximum Service TemperatureUnknown
Chemical Composition
C
0 to 0.015%
CR
20 to 22.5%
NI
49 to 63%
MO
12.5 to 14.5%
MN
0 to 0.5%
SI
0 to 0.080%
P
0 to 0.020%
S
0 to 0.010%
CU
0 to 0.5%
V
0 to 0.35%
CO
0 to 2.5%
W
2.5 to 3.5%
RES.
Residuals res. | | 0 to 0.5%
RESIDUALS RES.
0 to 0.5%
FE
2.0 to 6.0%
Mechanical
Elastic (Young's, Tensile) Modulus
220 GPa
Elongation at Break
28 %
Poisson's Ratio
0.29
Shear Modulus
84 GPa
Tensile Strength: Ultimate (UTS)
790 MPa
Physical
Density
8.9 g/cm 3
Thermal
Latent Heat of Fusion
320 J/g
Melting Completion (Liquidus)
1550 °C
Melting Onset (Solidus)
1490 °C
Specific Heat Capacity
420 J/kg-K
Thermal Conductivity
10 W/m-K
Thermal Diffusivity
2.7 mm 2 /s
Thermal Expansion
12 µm/m-K
Thermal Shock Resistance
21 points
Electrical
Electrical Conductivity: Equal Volume
1.5 % IACS
Electrical Conductivity: Equal Weight (Specific)
1.5 % IACS
Calculated
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
23 points
Strength to Weight: Axial
25 points
Strength to Weight: Bending
21 points
Environmental
Base Metal Price
70 % relative
Embodied Carbon
12 kg CO 2 /kg material
Embodied Energy
160 MJ/kg
Embodied Energy
160 MJ/kg 71 x 10 3 BTU/lb
Embodied Water
300 L/kg
Embodied Water
300 L/kg 35 gal/lb
Registered Designations & Aliases
AWS ERNiCrMo-10 Weld Metal