AWS ERNiCrFe-5 (N06062) Weld Metal
Nickel Welding & Filler Materials
Property Overview
Density8.5g/cm³
Elastic Modulus190GPa
Tensile Strength630MPa
Yield StrengthUnknown
Brinell HardnessUnknown
Maximum Service TemperatureUnknown
Chemical Composition
C
0 to 0.080%
CR
14 to 17%
NI
70 to 78.5%
MN
0 to 1.0%
SI
0 to 0.35%
P
0 to 0.030%
S
0 to 0.015%
CU
0 to 0.5%
NB
1.5 to 3.0%
CO
0 to 0.12%
RES.
Residuals res. | | 0 to 0.5%
RESIDUALS RES.
0 to 0.5%
FE
6.0 to 10%
Mechanical
Elastic (Young's, Tensile) Modulus
190 GPa
Elongation at Break
34 %
Poisson's Ratio
0.3
Shear Modulus
74 GPa
Tensile Strength: Ultimate (UTS)
630 MPa
Physical
Density
8.5 g/cm 3
Thermal
Latent Heat of Fusion
310 J/g
Melting Completion (Liquidus)
1390 °C
Melting Onset (Solidus)
1340 °C
Specific Heat Capacity
450 J/kg-K
Thermal Conductivity
14 W/m-K
Thermal Diffusivity
3.6 mm 2 /s
Thermal Expansion
12 µm/m-K
Thermal Shock Resistance
19 points
Electrical
Electrical Conductivity: Equal Volume
1.6 % IACS
Electrical Conductivity: Equal Weight (Specific)
1.7 % IACS
Calculated
Stiffness to Weight: Axial
12 points
Stiffness to Weight: Bending
23 points
Strength to Weight: Axial
20 points
Strength to Weight: Bending
19 points
Environmental
Base Metal Price
65 % relative
Embodied Carbon
11 kg CO 2 /kg material
Embodied Energy
150 MJ/kg
Embodied Energy
150 MJ/kg 66 x 10 3 BTU/lb
Embodied Water
250 L/kg
Embodied Water
250 L/kg 30 gal/lb
Registered Designations & Aliases
AWS ERNiCrFe-5 (N06062) Weld MetalN06062