AWS ERNiCrFe-11 Weld Metal
Nickel Welding & Filler Materials
Property Overview
Density8.2g/cm³
Elastic Modulus200GPa
Tensile Strength740MPa
Yield StrengthUnknown
Brinell HardnessUnknown
Maximum Service TemperatureUnknown
Chemical Composition
C
0 to 0.1%
CR
21 to 25%
NI
58 to 63%
MN
0 to 1.0%
SI
0 to 0.5%
P
0 to 0.030%
S
0 to 0.015%
CU
0 to 1.0%
AL
1.0 to 1.7%
RES.
Residuals res. | | 0 to 0.5%
RESIDUALS RES.
0 to 0.5%
FE
7.2 to 20%
Mechanical
Elastic (Young's, Tensile) Modulus
200 GPa
Elongation at Break
47 %
Poisson's Ratio
0.28
Shear Modulus
76 GPa
Tensile Strength: Ultimate (UTS)
740 MPa
Physical
Density
8.2 g/cm 3
Thermal
Latent Heat of Fusion
320 J/g
Melting Completion (Liquidus)
1360 °C
Melting Onset (Solidus)
1310 °C
Specific Heat Capacity
470 J/kg-K
Thermal Conductivity
11 W/m-K
Thermal Diffusivity
2.9 mm 2 /s
Thermal Expansion
13 µm/m-K
Thermal Shock Resistance
20 points
Electrical
Electrical Conductivity: Equal Volume
1.5 % IACS
Electrical Conductivity: Equal Weight (Specific)
1.6 % IACS
Calculated
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
23 points
Strength to Weight: Axial
25 points
Strength to Weight: Bending
22 points
Environmental
Base Metal Price
49 % relative
Embodied Carbon
8.0 kg CO 2 /kg material
Embodied Energy
110 MJ/kg
Embodied Energy
110 MJ/kg 49 x 10 3 BTU/lb
Embodied Water
280 L/kg
Embodied Water
280 L/kg 33 gal/lb
Registered Designations & Aliases
AWS ERNiCrFe-11 Weld Metal