AWS ERNiCr-3 (N06082) Weld Metal
Nickel Welding & Filler Materials
Property Overview
Density8.4g/cm³
Elastic Modulus190GPa
Tensile Strength630MPa
Yield StrengthUnknown
Brinell HardnessUnknown
Maximum Service TemperatureUnknown
Chemical Composition
C
0 to 0.1%
CR
18 to 22%
NI
67 to 77.5%
MN
2.5 to 3.5%
SI
0 to 0.5%
P
0 to 0.030%
S
0 to 0.015%
CU
0 to 0.5%
NB
2.0 to 3.0%
TI
0 to 0.75%
CO
0 to 0.12%
RES.
Residuals res. | | 0 to 0.5%
RESIDUALS RES.
0 to 0.5%
FE
0 to 3.0%
Mechanical
Elastic (Young's, Tensile) Modulus
190 GPa
Elongation at Break
34 %
Poisson's Ratio
0.29
Shear Modulus
75 GPa
Tensile Strength: Ultimate (UTS)
630 MPa
Physical
Density
8.4 g/cm 3
Thermal
Latent Heat of Fusion
320 J/g
Melting Completion (Liquidus)
1380 °C
Melting Onset (Solidus)
1330 °C
Specific Heat Capacity
460 J/kg-K
Thermal Expansion
13 µm/m-K
Thermal Shock Resistance
18 points
Calculated
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
23 points
Strength to Weight: Axial
21 points
Strength to Weight: Bending
19 points
Environmental
Base Metal Price
70 % relative
Embodied Carbon
11 kg CO 2 /kg material
Embodied Energy
160 MJ/kg
Embodied Energy
160 MJ/kg 70 x 10 3 BTU/lb
Embodied Water
280 L/kg
Embodied Water
280 L/kg 33 gal/lb
Registered Designations & Aliases
AWS ERNiCr-3 (N06082) Weld MetalN06082