AWS ENiCrMo-4 (W80276) Weld Metal
Nickel Welding & Filler Materials
Property Overview
Density9g/cm³
Elastic Modulus220GPa
Tensile Strength790MPa
Yield StrengthUnknown
Brinell HardnessUnknown
Maximum Service TemperatureUnknown
Chemical Composition
C
0 to 0.020%
CR
14.5 to 16.5%
NI
49.9 to 63.5%
MO
15 to 17%
MN
0 to 1.0%
SI
0 to 0.2%
P
0 to 0.040%
S
0 to 0.030%
CU
0 to 0.5%
V
0 to 0.35%
CO
0 to 2.5%
W
3.0 to 4.5%
RES.
Residuals res. | | 0 to 0.5%
RESIDUALS RES.
0 to 0.5%
FE
4.0 to 7.0%
Mechanical
Elastic (Young's, Tensile) Modulus
220 GPa
Elongation at Break
28 %
Poisson's Ratio
0.29
Shear Modulus
84 GPa
Tensile Strength: Ultimate (UTS)
790 MPa
Physical
Density
9.0 g/cm 3
Thermal
Latent Heat of Fusion
320 J/g
Melting Completion (Liquidus)
1590 °C
Melting Onset (Solidus)
1530 °C
Specific Heat Capacity
410 J/kg-K
Thermal Expansion
12 µm/m-K
Thermal Shock Resistance
22 points
Calculated
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
22 points
Strength to Weight: Axial
24 points
Strength to Weight: Bending
21 points
Environmental
Base Metal Price
70 % relative
Embodied Carbon
13 kg CO 2 /kg material
Embodied Energy
170 MJ/kg
Embodied Energy
170 MJ/kg 74 x 10 3 BTU/lb
Embodied Water
280 L/kg
Embodied Water
280 L/kg 34 gal/lb
Registered Designations & Aliases
AWS ENiCrMo-4 (W80276) Weld MetalW80276