AWS ENiCrMo-3 (W86112) Weld Metal
Nickel Welding & Filler Materials
Property Overview
Density8.6g/cm³
Elastic Modulus200GPa
Tensile Strength870MPa
Yield StrengthUnknown
Brinell HardnessUnknown
Maximum Service TemperatureUnknown
Chemical Composition
C
0 to 0.1%
CR
20 to 23%
NI
55 to 68.9%
MO
8.0 to 10%
MN
0 to 1.0%
SI
0 to 0.75%
P
0 to 0.030%
S
0 to 0.020%
CU
0 to 0.5%
NB
3.2 to 4.2%
CO
0 to 0.12%
RES.
Residuals res. | | 0 to 0.5%
RESIDUALS RES.
0 to 0.5%
FE
0 to 7.0%
Mechanical
Elastic (Young's, Tensile) Modulus
200 GPa
Elongation at Break
34 %
Poisson's Ratio
0.29
Shear Modulus
79 GPa
Tensile Strength: Ultimate (UTS)
870 MPa
Physical
Density
8.6 g/cm 3
Thermal
Latent Heat of Fusion
330 J/g
Melting Completion (Liquidus)
1480 °C
Melting Onset (Solidus)
1430 °C
Specific Heat Capacity
440 J/kg-K
Thermal Conductivity
11 W/m-K
Thermal Diffusivity
2.8 mm 2 /s
Thermal Expansion
12 µm/m-K
Thermal Shock Resistance
25 points
Electrical
Electrical Conductivity: Equal Volume
1.3 % IACS
Electrical Conductivity: Equal Weight (Specific)
1.4 % IACS
Calculated
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
23 points
Strength to Weight: Axial
28 points
Strength to Weight: Bending
24 points
Environmental
Base Metal Price
80 % relative
Embodied Carbon
14 kg CO 2 /kg material
Embodied Energy
190 MJ/kg
Embodied Energy
190 MJ/kg 82 x 10 3 BTU/lb
Embodied Water
290 L/kg
Embodied Water
290 L/kg 34 gal/lb
Registered Designations & Aliases
AWS ENiCrMo-3 (W86112) Weld MetalW86112