AWS ENiCrFe-2 (W86133) Weld Metal
Nickel Welding & Filler Materials
Property Overview
Density8.5g/cm³
Elastic Modulus190GPa
Tensile Strength790MPa
Yield StrengthUnknown
Brinell HardnessUnknown
Maximum Service TemperatureUnknown
Chemical Composition
C
0 to 0.1%
CR
13 to 17%
NI
62 to 85%
MO
0.5 to 2.5%
MN
1.0 to 3.5%
SI
0 to 0.75%
P
0 to 0.030%
S
0 to 0.020%
CU
0 to 0.5%
NB
0.5 to 4.0%
CO
0 to 0.12%
RES.
Residuals res. | | 0 to 0.5%
RESIDUALS RES.
0 to 0.5%
FE
0 to 12%
Mechanical
Elastic (Young's, Tensile) Modulus
190 GPa
Elongation at Break
28 %
Poisson's Ratio
0.3
Shear Modulus
74 GPa
Tensile Strength: Ultimate (UTS)
790 MPa
Physical
Density
8.5 g/cm 3
Thermal
Latent Heat of Fusion
310 J/g
Melting Completion (Liquidus)
1390 °C
Melting Onset (Solidus)
1350 °C
Specific Heat Capacity
450 J/kg-K
Thermal Expansion
12 µm/m-K
Thermal Shock Resistance
24 points
Calculated
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
23 points
Strength to Weight: Axial
26 points
Strength to Weight: Bending
22 points
Environmental
Base Metal Price
65 % relative
Embodied Carbon
11 kg CO 2 /kg material
Embodied Energy
160 MJ/kg
Embodied Energy
160 MJ/kg 68 x 10 3 BTU/lb
Embodied Water
260 L/kg
Embodied Water
260 L/kg 31 gal/lb
Registered Designations & Aliases
AWS ENiCrFe-2 (W86133) Weld MetalW86133