AWS ENiCrCoMo-1 (W86117) Weld Metal
Nickel Welding & Filler Materials
Property Overview
Density8.5g/cm³
Elastic Modulus210GPa
Tensile Strength710MPa
Yield StrengthUnknown
Brinell HardnessUnknown
Maximum Service TemperatureUnknown
Chemical Composition
C
0.050 to 0.15%
CR
21 to 26%
NI
38.6 to 61.7%
MO
8.0 to 10%
MN
0.3 to 2.5%
SI
0 to 0.75%
P
0 to 0.030%
S
0 to 0.015%
CU
0 to 0.5%
NB
0 to 1.0%
CO
9.0 to 15%
RES.
Residuals res. | | 0 to 0.5%
RESIDUALS RES.
0 to 0.5%
FE
0 to 5.0%
Mechanical
Elastic (Young's, Tensile) Modulus
210 GPa
Elongation at Break
28 %
Poisson's Ratio
0.29
Shear Modulus
82 GPa
Tensile Strength: Ultimate (UTS)
710 MPa
Physical
Density
8.5 g/cm 3
Thermal
Latent Heat of Fusion
330 J/g
Melting Completion (Liquidus)
1430 °C
Melting Onset (Solidus)
1380 °C
Specific Heat Capacity
440 J/kg-K
Thermal Expansion
13 µm/m-K
Thermal Shock Resistance
19 points
Calculated
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
23 points
Strength to Weight: Axial
23 points
Strength to Weight: Bending
21 points
Environmental
Base Metal Price
75 % relative
Embodied Carbon
11 kg CO 2 /kg material
Embodied Energy
140 MJ/kg
Embodied Energy
140 MJ/kg 62 x 10 3 BTU/lb
Embodied Water
340 L/kg
Embodied Water
340 L/kg 40 gal/lb
Registered Designations & Aliases
AWS ENiCrCoMo-1 (W86117) Weld MetalW86117