7010 (AlZn6MgCu, A97010) Aluminum
Wrought Aluminum Alloys
T6
Property Overview
Density3g/cm³
Elastic Modulus70GPa
Tensile Strength590MPa
Yield Strength530MPa
Brinell Hardness190HB
Maximum Service Temperature200°C
Chemical Composition
CR
0 to 0.050%
NI
0 to 0.050%
MN
0 to 0.1%
SI
0 to 0.12%
CU
1.5 to 2.0%
TI
0 to 0.060%
AL
87.9 to 90.6%
MG
2.1 to 2.6%
RES.
Residuals res. | | 0 to 0.15%
RESIDUALS RES.
0 to 0.15%
ZN
5.7 to 6.7%
ZR
0.1 to 0.16%
FE
0 to 0.15%
Mechanical
Elastic (Young's, Tensile) Modulus
70 GPa
Elongation at Break
4.0 %
Fatigue Strength
180 MPa
Poisson's Ratio
0.32
Shear Modulus
26 GPa
Shear Strength
340 MPa
Tensile Strength: Ultimate (UTS)
590 MPa
Tensile Strength: Yield (Proof)
530 MPa
Hardness
Brinell Hardness
190
Physical
Density
3.0 g/cm 3
Thermal
Latent Heat of Fusion
380 J/g
Maximum Temperature: Mechanical
200 °C
Melting Completion (Liquidus)
630 °C
Melting Onset (Solidus)
480 °C
Specific Heat Capacity
860 J/kg-K
Thermal Conductivity
150 W/m-K
Thermal Diffusivity
58 mm 2 /s
Thermal Expansion
24 µm/m-K
Thermal Shock Resistance
26 points
Electrical
Electrical Conductivity: Equal Volume
40 % IACS
Electrical Conductivity: Equal Weight (Specific)
120 % IACS
Calculated
Resilience: Ultimate (Unit Rupture Work)
23 MJ/m 3
Resilience: Unit (Modulus of Resilience)
2050 kJ/m 3
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
45 points
Strength to Weight: Axial
54 points
Strength to Weight: Bending
52 points
Environmental
Base Metal Price
10 % relative
Embodied Carbon
8.3 kg CO 2 /kg material
Embodied Energy
150 MJ/kg
Embodied Energy
150 MJ/kg 64 x 10 3 BTU/lb
Embodied Water
1120 L/kg
Embodied Water
1120 L/kg 130 gal/lb
Registered Designations & Aliases
7010 (AlZn6MgCu, A97010) AluminumA97010AlZn6MgCuEN AW-7010
Standards
EN 485-2 EN 485-2: Aluminium and aluminium alloys. Sheet, strip and plate. Mechanical properties
EN 573-3 EN 573-3: Aluminium and aluminium alloys. Chemical composition and form of wrought products. Chemical composition and form of products
ISO 6361-2 ISO 6361-2: Wrought aluminium and aluminium alloys - Sheets, strips and plates - Part 2: Mechanical properties