Grade M35-2 (J04020) Cast Nickel
Nickel Alloys
Property Overview
Density8.8g/cm³
Elastic Modulus160GPa
Tensile Strength500MPa
Yield Strength230MPa
Brinell HardnessUnknown
Maximum Service Temperature900°C
Chemical Composition
C
0 to 0.35%
NI
59.1 to 74%
MN
0 to 1.5%
SI
0 to 2.0%
P
0 to 0.030%
S
0 to 0.030%
CU
26 to 33%
NB
0 to 0.5%
FE
0 to 3.5%
Mechanical
Elastic (Young's, Tensile) Modulus
160 GPa
Elongation at Break
28 %
Fatigue Strength
160 MPa
Poisson's Ratio
0.32
Shear Modulus
62 GPa
Tensile Strength: Ultimate (UTS)
500 MPa
Tensile Strength: Yield (Proof)
230 MPa
Physical
Density
8.8 g/cm 3
Thermal
Latent Heat of Fusion
280 J/g
Maximum Temperature: Mechanical
900 °C
Melting Completion (Liquidus)
1280 °C
Melting Onset (Solidus)
1230 °C
Specific Heat Capacity
430 J/kg-K
Thermal Conductivity
22 W/m-K
Thermal Diffusivity
5.7 mm 2 /s
Thermal Expansion
13 µm/m-K
Thermal Shock Resistance
17 points
Electrical
Electrical Conductivity: Equal Volume
3.3 % IACS
Electrical Conductivity: Equal Weight (Specific)
3.4 % IACS
Calculated
Resilience: Ultimate (Unit Rupture Work)
120 MJ/m 3
Resilience: Unit (Modulus of Resilience)
170 kJ/m 3
Stiffness to Weight: Axial
10 points
Stiffness to Weight: Bending
21 points
Strength to Weight: Axial
16 points
Strength to Weight: Bending
16 points
Environmental
Base Metal Price
55 % relative
Embodied Carbon
8.1 kg CO 2 /kg material
Embodied Energy
110 MJ/kg
Embodied Energy
110 MJ/kg 49 x 10 3 BTU/lb
Embodied Water
250 L/kg
Embodied Water
250 L/kg 30 gal/lb
Registered Designations & Aliases
Grade M35-2 (J04020) Cast NickelJ04020
Standards
ASTM A494 ASTM A494: Standard Specification for Castings, Nickel and Nickel Alloy
ASTM A494 ASTM A494: Standard Specification for Castings, Nickel and Nickel Alloy Welding Metallurgy and Weldability of Nickel-Base Alloys, John C. Lippold et al., 2009 Engineering Properties of Nickel and Nickel Alloys, John L. Everhart, 1971 Nickel Alloys, Ulrich Heubner (editor), 1998