ZK60A-F Magnesium
Magnesium Alloys
Property Overview
Density1.9g/cm³
Elastic Modulus46GPa
Tensile Strength320MPa
Yield Strength230MPa
Brinell HardnessUnknown
Maximum Service Temperature120°C
Chemical Composition
MG
92.5 to 94.8%
RES.
Residuals res. | | 0 to 0.3%
RESIDUALS RES.
0 to 0.3%
ZN
4.8 to 6.2%
ZR
0.45 to 1.0%
Mechanical
Elastic (Young's, Tensile) Modulus
46 GPa
Elongation at Break
7.2 %
Fatigue Strength
160 MPa
Poisson's Ratio
0.29
Shear Modulus
18 GPa
Shear Strength
190 MPa
Tensile Strength: Ultimate (UTS)
320 MPa
Tensile Strength: Yield (Proof)
230 MPa
Physical
Density
1.9 g/cm 3
Thermal
Latent Heat of Fusion
330 J/g
Maximum Temperature: Mechanical
120 °C
Melting Completion (Liquidus)
600 °C
Melting Onset (Solidus)
550 °C
Specific Heat Capacity
960 J/kg-K
Thermal Conductivity
120 W/m-K
Thermal Diffusivity
66 mm 2 /s
Thermal Expansion
26 µm/m-K
Thermal Shock Resistance
19 points
Electrical
Electrical Conductivity: Equal Volume
29 % IACS
Electrical Conductivity: Equal Weight (Specific)
140 % IACS
Calculated
Resilience: Ultimate (Unit Rupture Work)
21 MJ/m 3
Resilience: Unit (Modulus of Resilience)
600 kJ/m 3
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
63 points
Strength to Weight: Axial
47 points
Strength to Weight: Bending
55 points
Environmental
Base Metal Price
13 % relative
Embodied Carbon
23 kg CO 2 /kg material
Embodied Energy
160 MJ/kg
Embodied Energy
160 MJ/kg 70 x 10 3 BTU/lb
Embodied Water
940 L/kg
Embodied Water
940 L/kg 110 gal/lb
Registered Designations & Aliases
ZK60A-F Magnesium
Standards
ASTM B107 ASTM B107: Standard Specification for Magnesium-Alloy Extruded Bars, Rods, Profiles, Tubes, and Wire
ASTM B107 ASTM B107: Standard Specification for Magnesium-Alloy Extruded Bars, Rods, Profiles, Tubes, and Wire Advances in Wrought Magnesium Alloys: Fundamentals of Processing, Properties and Applications, Colleen Bettles and Matthew Barnett (editors), 2012 ASTM B91: Standard Specification for Magnesium-Alloy Forgings Essential Readings in Magnesium Technology, Suveen N. Mathaudhu et al. (editors), 2014 Properties and Selection: Nonferrous Alloys and Special-Purpose Materials, ASM Handbook vol. 2, ASM International, 1993
ASTM B91 ASTM B91: Standard Specification for Magnesium-Alloy Forgings