UNS S35135 (Alloy 864) Stainless Steel
Austenitic & General Stainless Steels
Property Overview
Density8.1g/cm³
Elastic Modulus200GPa
Tensile Strength590MPa
Yield Strength230MPa
Brinell HardnessUnknown
Maximum Service Temperature1100°C
Chemical Composition
C
0 to 0.080%
CR
20 to 25%
NI
30 to 38%
MO
4.0 to 4.8%
MN
0 to 1.0%
SI
0.6 to 1.0%
P
0 to 0.045%
S
0 to 0.015%
CU
0 to 0.75%
TI
0.4 to 1.0%
FE
28.3 to 45%
Mechanical
Elastic (Young's, Tensile) Modulus
200 GPa
Elongation at Break
34 %
Fatigue Strength
180 MPa
Poisson's Ratio
0.28
Shear Modulus
79 GPa
Shear Strength
390 MPa
Tensile Strength: Ultimate (UTS)
590 MPa
Tensile Strength: Yield (Proof)
230 MPa
Physical
Density
8.1 g/cm 3
Thermal
Latent Heat of Fusion
320 J/g
Maximum Temperature: Corrosion
560 °C
Maximum Temperature: Mechanical
1100 °C
Melting Completion (Liquidus)
1430 °C
Melting Onset (Solidus)
1380 °C
Specific Heat Capacity
470 J/kg-K
Thermal Expansion
16 µm/m-K
Thermal Shock Resistance
13 points
Calculated
PREN (Pitting Resistance)
37
Resilience: Ultimate (Unit Rupture Work)
160 MJ/m 3
Resilience: Unit (Modulus of Resilience)
130 kJ/m 3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
24 points
Strength to Weight: Axial
20 points
Strength to Weight: Bending
19 points
Environmental
Base Metal Price
37 % relative
Embodied Carbon
6.8 kg CO 2 /kg material
Embodied Energy
94 MJ/kg
Embodied Energy
94 MJ/kg 41 x 10 3 BTU/lb
Embodied Water
220 L/kg
Embodied Water
220 L/kg 26 gal/lb
Registered Designations & Aliases
Alloy 864S35135UNS S35135 (Alloy 864) Stainless Steel
Standards
ASTM A240 ASTM A240: Standard Specification for Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip for Pressure Vessels and for General Applications
ASTM A240 ASTM A240: Standard Specification for Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip for Pressure Vessels and for General Applications Welding Metallurgy and Weldability of Stainless Steels, John C. Lippold and Damian J. Kotecki, 2005