EN 1.4854 (X6NiCrSiNCe35-25) Stainless Steel
Other Steels
Property Overview
Density7.9g/cm³
Elastic Modulus200GPa
Tensile Strength750MPa
Yield Strength300MPa
Brinell Hardness310HB
Maximum Service Temperature1170°C
Chemical Composition
C
0.040 to 0.080%
CR
24 to 26%
NI
34 to 36%
MN
0 to 2.0%
SI
1.2 to 2.0%
N
0.12 to 0.2%
P
0 to 0.040%
S
0 to 0.015%
CE
0.030 to 0.080%
FE
33.6 to 40.6%
Mechanical
A - Min. elongation at fracture (%) (+AT)
40
+AT
Elastic (Young's, Tensile) Modulus
200 GPa
Elongation at Break
45 %
Fatigue Strength
310 MPa
Poisson's Ratio
0.28
R p0.2 0.2% proof strength (MPa) (+AT)
300
+AT
Rm - Tensile strength (MPa) (+AT)
650-850
+AT
Shear Modulus
78 GPa
Shear Strength
520 MPa
Tensile Strength: Ultimate (UTS)
750 MPa
Tensile Strength: Yield (Proof)
340 MPa
Hardness
Brinell Hardness
180
Brinell hardness (HB): (+AT)
310
+AT
Physical
Density
7.9 g/cm 3
Thermal
Latent Heat of Fusion
330 J/g
Maximum Temperature: Corrosion
450 °C
Maximum Temperature: Mechanical
1170 °C
Melting Completion (Liquidus)
1370 °C
Melting Onset (Solidus)
1330 °C
Specific Heat Capacity
480 J/kg-K
Thermal Conductivity
11 W/m-K
Thermal Diffusivity
2.9 mm 2 /s
Thermal Expansion
15 µm/m-K
Thermal Shock Resistance
18 points
Electrical
Electrical Conductivity: Equal Volume
1.7 % IACS
Electrical Conductivity: Equal Weight (Specific)
2.0 % IACS
Calculated
PREN (Pitting Resistance)
28
Resilience: Ultimate (Unit Rupture Work)
270 MJ/m 3
Resilience: Unit (Modulus of Resilience)
280 kJ/m 3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
25 points
Strength to Weight: Axial
26 points
Strength to Weight: Bending
23 points
Environmental
Base Metal Price
34 % relative
Embodied Carbon
5.7 kg CO 2 /kg material
Embodied Energy
81 MJ/kg
Embodied Energy
81 MJ/kg 35 x 10 3 BTU/lb
Embodied Water
220 L/kg
Embodied Water
220 L/kg 26 gal/lb
Registered Designations & Aliases
1.48541.4854EN 1.4854 (X6NiCrSiNCe35-25) Stainless SteelX6NiCrSiNCe35-25X6NiCrSiNCe35-25
Standards
EN 10088-1 EN 10088-1: 2005 Stainless steels. List of stainless steels
EN 10088-1 EN 10088-1: Stainless steels - Part 1: List of stainless steels
EN 10095 EN 10095: 1999 Heat Resisting Steels and Nickel Alloys
EN 10095 EN 10095: Heat resisting steels and nickel alloys
EN 10095 EN 10095: Heat resisting steels and nickel alloys EN 10088-1: Stainless steels - Part 1: List of stainless steels
EN 10296-2 EN 10296-2: 2005 Welded circular steel tubes for mechanical and general engineering purposes. Stainless steel. Technical delivery conditions
EN 10297-2 EN 10297-2: 2005 Seamless circular steel tubes for mechanical and general engineering purposes. Stainless steel. Technical delivery conditions