EN 1.4112 (X90CrMoV18) Stainless Steel
Martensitic Stainless Steels
Property Overview
Density7.7g/cm³
Elastic Modulus200GPa
Tensile Strength750MPa
Yield Strength430MPa
Brinell Hardness265HB
Maximum Service Temperature910°C
Chemical Composition
C
0.85 to 1.0%
CR
17 to 19%
MO
0.9 to 1.3%
MN
0 to 1.0%
SI
0 to 1.0%
P
0 to 0.040%
S
0 to 0.015%
V
0.070 to 0.12%
FE
76.6 to 81.2%
Mechanical
Elastic (Young's, Tensile) Modulus
200 GPa
Elongation at Break
20 %
Fatigue Strength
280 MPa
Poisson's Ratio
0.28
Shear Modulus
77 GPa
Shear Strength
470 MPa
Tensile Strength: Ultimate (UTS)
750 MPa
Tensile Strength: Yield (Proof)
430 MPa
Hardness
+A Soft annealed +AC Annealed to achieve spheroidization of the carbides +AR As rolled +AT Solution annealed +C Cold drawn / hard +CR Cold rolled +FP Treated to ferrite-pearlite structure and hardness range +I Isothermal annealing +LC Cold drawn / soft +M Thermo mechanical rolling +N Normalized +NT Normalized and tempered
+P Precipitation hardened +PE Peeled +QA Air quenched and tempered +QL Liquid quenched and tempered +QT Quenched and tempered +S Treated to improve shearability +SH As rolled and turned +SR Cold drawn and stress relieved +T Tempered +TH Treated to hardness range +WW Warm worked +U Untreated
+A
Brinell Hardness
230
Brinell hardness (HB): (+A)
265
+A
Physical
Density
7.7 g/cm 3
Thermal
Latent Heat of Fusion
280 J/g
Maximum Temperature: Corrosion
400 °C
Maximum Temperature: Mechanical
910 °C
Melting Completion (Liquidus)
1430 °C
Melting Onset (Solidus)
1390 °C
Specific Heat Capacity
480 J/kg-K
Thermal Conductivity
15 W/m-K
Thermal Diffusivity
4.1 mm 2 /s
Thermal Expansion
10 µm/m-K
Thermal Shock Resistance
26 points
Electrical
Electrical Conductivity: Equal Volume
2.2 % IACS
Electrical Conductivity: Equal Weight (Specific)
2.5 % IACS
Calculated
PREN (Pitting Resistance)
22
Resilience: Ultimate (Unit Rupture Work)
130 MJ/m 3
Resilience: Unit (Modulus of Resilience)
480 kJ/m 3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
25 points
Strength to Weight: Axial
27 points
Strength to Weight: Bending
24 points
Environmental
Base Metal Price
10 % relative
Embodied Carbon
2.6 kg CO 2 /kg material
Embodied Energy
37 MJ/kg
Embodied Energy
37 MJ/kg 16 x 10 3 BTU/lb
Embodied Water
130 L/kg
Embodied Water
130 L/kg 15 gal/lb
Registered Designations & Aliases
1.41121.4112EN 1.4112 (X90CrMoV18) Stainless SteelX90CrMoV18X90CrMoV18
Standards
EN 10088-1 EN 10088-1: 2005 Stainless steels. List of stainless steels
EN 10088-1 EN 10088-1: Stainless steels - Part 1: List of stainless steels
EN 10088-3 EN 10088-3: 2005 Stainless steels. Technical delivery conditions for semi-finished products, bars, rods, wire, sections and bright products of corrosion resisting steels for general purposes
EN 10088-3 EN 10088-3: Stainless steels - Part 3: Technical delivery conditions for semi-finished products, bars, rods, wire, sections and bright products of corrosion resisting steels for general purposes