EN 1.3549 (X89CrMoV18-1) Stainless Bearing Steel
Martensitic Stainless Steels
Property Overview
Density7.7g/cm³
Elastic Modulus200GPa
Tensile Strength730MPa
Yield StrengthUnknown
Brinell Hardness220HB
Maximum Service Temperature910°C
Chemical Composition
C
0.85 to 1.0%
CR
17 to 19%
MO
0.9 to 1.3%
MN
0 to 1.0%
SI
0 to 1.0%
P
0 to 0.040%
S
0 to 0.030%
V
0.070 to 0.12%
FE
77.5 to 82%
Mechanical
Elastic (Young's, Tensile) Modulus
200 GPa
Poisson's Ratio
0.28
Shear Modulus
77 GPa
Tensile Strength: Ultimate (UTS)
730 MPa
Hardness
Brinell Hardness
220
Physical
Density
7.7 g/cm 3
Thermal
Latent Heat of Fusion
280 J/g
Maximum Temperature: Corrosion
400 °C
Maximum Temperature: Mechanical
910 °C
Melting Completion (Liquidus)
1430 °C
Melting Onset (Solidus)
1390 °C
Specific Heat Capacity
480 J/kg-K
Thermal Conductivity
21 W/m-K
Thermal Diffusivity
5.6 mm 2 /s
Thermal Expansion
10 µm/m-K
Thermal Shock Resistance
26 points
Electrical
Electrical Conductivity: Equal Volume
2.3 % IACS
Electrical Conductivity: Equal Weight (Specific)
2.7 % IACS
Calculated
PREN (Pitting Resistance)
22
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
25 points
Strength to Weight: Axial
27 points
Strength to Weight: Bending
24 points
Environmental
Base Metal Price
10 % relative
Embodied Carbon
2.6 kg CO 2 /kg material
Embodied Energy
37 MJ/kg
Embodied Energy
37 MJ/kg 16 x 10 3 BTU/lb
Embodied Water
130 L/kg
Embodied Water
130 L/kg 15 gal/lb
Registered Designations & Aliases
1.3549EN 1.3549 (X89CrMoV18-1) Stainless Bearing SteelX89CrMoV18-1
Standards
ISO 683-17 ISO 683-17: Heat-treated steels, alloy steels and free-cutting steels - Part 17: Ball and roller bearing steels
ISO 683-17 ISO 683-17: Heat-treated steels, alloy steels and free-cutting steels - Part 17: Ball and roller bearing steels Corrosion of Stainless Steels, A. John Sedriks, 1996