UNS S42035 Stainless Steel
Ferritic Stainless Steels
Property Overview
Density7.8g/cm³
Elastic Modulus200GPa
Tensile Strength630MPa
Yield Strength430MPa
Brinell Hardness160HB
Maximum Service Temperature810°C
Chemical Composition
C
0 to 0.080%
CR
13.5 to 15.5%
NI
1.0 to 2.5%
MO
0.2 to 1.2%
MN
0 to 1.0%
SI
0 to 1.0%
P
0 to 0.045%
S
0 to 0.030%
TI
0.3 to 0.5%
FE
78.1 to 85%
Mechanical
Elastic (Young's, Tensile) Modulus
200 GPa
Elongation at Break
18 %
Fatigue Strength
260 MPa
Poisson's Ratio
0.28
Shear Modulus
77 GPa
Shear Strength
390 MPa
Tensile Strength: Ultimate (UTS)
630 MPa
Tensile Strength: Yield (Proof)
430 MPa
Hardness
Brinell Hardness
160
Rockwell B Hardness
76
Physical
Density
7.8 g/cm 3
Thermal
Latent Heat of Fusion
280 J/g
Maximum Temperature: Corrosion
470 °C
Maximum Temperature: Mechanical
810 °C
Melting Completion (Liquidus)
1450 °C
Melting Onset (Solidus)
1400 °C
Specific Heat Capacity
480 J/kg-K
Thermal Conductivity
27 W/m-K
Thermal Diffusivity
7.2 mm 2 /s
Thermal Expansion
10 µm/m-K
Thermal Shock Resistance
22 points
Electrical
Electrical Conductivity: Equal Volume
2.7 % IACS
Electrical Conductivity: Equal Weight (Specific)
3.2 % IACS
Calculated
PREN (Pitting Resistance)
17
Resilience: Ultimate (Unit Rupture Work)
100 MJ/m 3
Resilience: Unit (Modulus of Resilience)
460 kJ/m 3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
25 points
Strength to Weight: Axial
22 points
Strength to Weight: Bending
21 points
Environmental
Base Metal Price
9.5 % relative
Embodied Carbon
2.4 kg CO 2 /kg material
Embodied Energy
34 MJ/kg
Embodied Energy
34 MJ/kg 15 x 10 3 BTU/lb
Embodied Water
110 L/kg
Embodied Water
110 L/kg 14 gal/lb
Registered Designations & Aliases
S42035UNS S42035 Stainless Steel
Standards
ASTM A240 ASTM A240: Standard Specification for Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip for Pressure Vessels and for General Applications
ASTM A240 ASTM A240: Standard Specification for Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip for Pressure Vessels and for General Applications Welding Metallurgy and Weldability of Stainless Steels, John C. Lippold and Damian J. Kotecki, 2005 ASTM A959: Standard Guide for Specifying Harmonized Standard Grade Compositions for Wrought Stainless Steels Corrosion of Stainless Steels, A. John Sedriks, 1996
ASTM A959 ASTM A959: Standard Guide for Specifying Harmonized Standard Grade Compositions for Wrought Stainless Steels