6025 (AlMg2.5SiMnCu, A96025) Aluminum
Wrought Aluminum Alloys
annealed
Property Overview
Density2.8g/cm³
Elastic Modulus70GPa
Tensile Strength190MPa
Yield Strength68MPa
Brinell HardnessUnknown
Maximum Service Temperature160°C
Chemical Composition
CR
0 to 0.2%
MN
0.6 to 1.4%
SI
0.8 to 1.5%
CU
0.2 to 0.7%
TI
0 to 0.2%
AL
91.7 to 96.3%
MG
2.1 to 3.0%
RES.
Residuals res. | | 0 to 0.15%
RESIDUALS RES.
0 to 0.15%
ZN
0 to 0.5%
FE
0 to 0.7%
Mechanical
Elastic (Young's, Tensile) Modulus
70 GPa
Elongation at Break
10 %
Fatigue Strength
67 MPa
Poisson's Ratio
0.33
Shear Modulus
26 GPa
Shear Strength
110 MPa
Tensile Strength: Ultimate (UTS)
190 MPa
Tensile Strength: Yield (Proof)
68 MPa
Physical
Density
2.8 g/cm 3
Thermal
Latent Heat of Fusion
410 J/g
Maximum Temperature: Mechanical
160 °C
Melting Completion (Liquidus)
650 °C
Melting Onset (Solidus)
550 °C
Specific Heat Capacity
900 J/kg-K
Thermal Conductivity
130 W/m-K
Thermal Diffusivity
54 mm 2 /s
Thermal Expansion
23 µm/m-K
Thermal Shock Resistance
8.2 points
Electrical
Electrical Conductivity: Equal Volume
33 % IACS
Electrical Conductivity: Equal Weight (Specific)
110 % IACS
Calculated
Resilience: Ultimate (Unit Rupture Work)
15 MJ/m 3
Resilience: Unit (Modulus of Resilience)
33 kJ/m 3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
50 points
Strength to Weight: Axial
19 points
Strength to Weight: Bending
26 points
Environmental
Base Metal Price
9.5 % relative
Embodied Carbon
8.5 kg CO 2 /kg material
Embodied Energy
150 MJ/kg
Embodied Energy
150 MJ/kg 65 x 10 3 BTU/lb
Embodied Water
1160 L/kg
Embodied Water
1160 L/kg 140 gal/lb
Registered Designations & Aliases
6025 (AlMg2.5SiMnCu, A96025) AluminumA96025AlMg2.5SiMnCuEN AW-6025
Standards
EN 485-2 EN 485-2: Aluminium and aluminium alloys. Sheet, strip and plate. Mechanical properties
EN 573-3 EN 573-3: Aluminium and aluminium alloys. Chemical composition and form of wrought products. Chemical composition and form of products
ISO 6361-2 ISO 6361-2: Wrought aluminium and aluminium alloys - Sheets, strips and plates - Part 2: Mechanical properties