EN 1.4511 (X3CrNb17) Stainless Steel
Ferritic Stainless Steels
Property Overview
Density7.7g/cm³
Elastic Modulus200GPa
Tensile Strength510MPa
Yield Strength260MPa
Brinell Hardness180HB
Maximum Service Temperature870°C
Mechanical
A - Min. elongation at fracture (%) (+A)
20-23
+A
Elastic (Young's, Tensile) Modulus
200 GPa
R p0.2 0.2% proof strength (MPa) (+A)
200-230
+A
Rm - Tensile strength (MPa) (+A)
420-620
+A
Tensile Strength: Ultimate (UTS)
510 MPa
Tensile Strength: Yield (Proof)
260 MPa
Hardness
+A Soft annealed +AC Annealed to achieve spheroidization of the carbides +AR As rolled +AT Solution annealed +C Cold drawn / hard +CR Cold rolled +FP Treated to ferrite-pearlite structure and hardness range +I Isothermal annealing +LC Cold drawn / soft +M Thermo mechanical rolling +N Normalized +NT Normalized and tempered
+P Precipitation hardened +PE Peeled +QA Air quenched and tempered +QL Liquid quenched and tempered +QT Quenched and tempered +S Treated to improve shearability +SH As rolled and turned +SR Cold drawn and stress relieved +T Tempered +TH Treated to hardness range +WW Warm worked +U Untreated
+A
Thermal
Latent Heat of Fusion
280 J/g
Maximum Temperature: Corrosion
480 °C
Maximum Temperature: Mechanical
870 °C
Melting Completion (Liquidus)
1440 °C
Melting Onset (Solidus)
1400 °C
Specific Heat Capacity
480 J/kg-K
Thermal Conductivity
25 W/m-K
Thermal Diffusivity
6.7 mm 2 /s
Thermal Expansion
10 µm/m-K
Thermal Shock Resistance
19 points
Electrical
Electrical Conductivity: Equal Volume
2.9 % IACS
Electrical Conductivity: Equal Weight (Specific)
3.3 % IACS
Calculated
PREN (Pitting Resistance)
17
Resilience: Ultimate (Unit Rupture Work)
110 MJ/m 3
Resilience: Unit (Modulus of Resilience)
170 kJ/m 3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
25 points
Strength to Weight: Axial
18 points
Strength to Weight: Bending
18 points
Environmental
Base Metal Price
11 % relative
Embodied Carbon
2.5 kg CO 2 /kg material
Embodied Energy
37 MJ/kg 16 x 10 3 BTU/lb
Embodied Water
120 L/kg 14 gal/lb
Registered Designations & Aliases
1.45111.4511EN 1.4511 (X3CrNb17) Stainless SteelX3CrNb17X3CrNb17
Standards
EN 10088-1 EN 10088-1: 2005 Stainless steels. List of stainless steels
EN 10088-1 EN 10088-1: Stainless steels - Part 1: List of stainless steels
EN 10088-2 EN 10088-2: 2005 Stainless steels. Technical delivery conditions for sheet/plate and strip of corrosion resisting steels for general purposes
EN 10088-2 EN 10088-2: Stainless steels - Part 2: Technical delivery conditions for sheet/plate and strip of corrosion resisting steels for general purposes
EN 10088-2 EN 10088-2: Stainless steels - Part 2: Technical delivery conditions for sheet/plate and strip of corrosion resisting steels for general purposes EN 10088-3: Stainless steels - Part 3: Technical delivery conditions for semi-finished products, bars, rods, wire, sections and bright products of corrosion resisting steels for general purposes EN 10088-1: Stainless steels - Part 1: List of stainless steels Welding Metallurgy of Stainless Steels, Erich Folkhard et al., 2012 Corrosion of Stainless Steels, A. John Sedriks, 1996
EN 10088-3 EN 10088-3: 2005 Stainless steels. Technical delivery conditions for semi-finished products, bars, rods, wire, sections and bright products of corrosion resisting steels for general purposes
EN 10088-3 EN 10088-3: Stainless steels - Part 3: Technical delivery conditions for semi-finished products, bars, rods, wire, sections and bright products of corrosion resisting steels for general purposes