SAE-AISI 1005 (G10050) Carbon Steel
Carbon & Non-Alloy Steels
Property Overview
Density7.9g/cm³
Elastic Modulus190GPa
Tensile Strength330MPa
Yield Strength260MPa
Brinell Hardness95HB
Maximum Service Temperature400°C
Chemical Composition
C
0 to 0.060%
MN
0 to 0.35%
P
0 to 0.040%
S
0 to 0.050%
FE
99.5 to 100%
Mechanical
Elastic (Young's, Tensile) Modulus
190 GPa
Elongation at Break
23 %
Fatigue Strength
190 MPa
Poisson's Ratio
0.29
Shear Modulus
73 GPa
Shear Strength
210 MPa
Tensile Strength: Ultimate (UTS)
330 MPa
Tensile Strength: Yield (Proof)
260 MPa
Hardness
Brinell Hardness
95
Physical
Density
7.9 g/cm 3
Thermal
Latent Heat of Fusion
250 J/g
Maximum Temperature: Mechanical
400 °C
Melting Completion (Liquidus)
1470 °C
Melting Onset (Solidus)
1430 °C
Specific Heat Capacity
470 J/kg-K
Thermal Conductivity
53 W/m-K
Thermal Diffusivity
14 mm 2 /s
Thermal Expansion
12 µm/m-K
Thermal Shock Resistance
10 points
Electrical
Electrical Conductivity: Equal Volume
6.9 % IACS
Electrical Conductivity: Equal Weight (Specific)
7.9 % IACS
Calculated
Resilience: Ultimate (Unit Rupture Work)
70 MJ/m 3
Resilience: Unit (Modulus of Resilience)
180 kJ/m 3
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
24 points
Strength to Weight: Axial
12 points
Strength to Weight: Bending
13 points
Environmental
Base Metal Price
1.8 % relative
Embodied Carbon
1.4 kg CO 2 /kg material
Embodied Energy
18 MJ/kg
Embodied Energy
18 MJ/kg 7.7 x 10 3 BTU/lb
Embodied Water
45 L/kg
Embodied Water
45 L/kg 5.4 gal/lb
Registered Designations & Aliases
G10050SAE-AISI 1005 (G10050) Carbon Steel
Standards
ASTM A29 ASTM A29: Standard Specification for Steel Bars, Carbon and Alloy, Hot-Wrought, General Requirements for