EN 1.1221 (C60E) Non-Alloy Steel

Other Steels

Material conditionannealed

Overview Chemical Composition Mechanical Properties Physical Properties Other Properties

Property Overview

Density7.8g/cm³

Elastic Modulus190GPa

Tensile Strength730MPa

Yield Strength410MPa

Brinell Hardness210HB

Maximum Service Temperature400°C

Weight Calculator

Chemical Composition

0.57 to 0.65%

0 to 0.4%

0 to 0.1%

0.6 to 0.9%

0 to 0.4%

0 to 0.035%

97.1 to 98.8%

Mechanical

Elastic (Young's, Tensile) Modulus

190 GPa

Elongation at Break

21 %

Fatigue Strength

280 MPa

Poisson's Ratio

0.29

Shear Modulus

72 GPa

Shear Strength

460 MPa

Tensile Strength: Ultimate (UTS)

730 MPa

Tensile Strength: Yield (Proof)

410 MPa

Hardness

Brinell Hardness

210

Physical

Density

7.8 g/cm 3

Thermal

Latent Heat of Fusion

250 J/g

Maximum Temperature: Mechanical

400 °C

Melting Completion (Liquidus)

1460 °C

Melting Onset (Solidus)

1410 °C

Specific Heat Capacity

470 J/kg-K

Thermal Conductivity

48 W/m-K

Thermal Diffusivity

13 mm 2 /s

Thermal Expansion

12 µm/m-K

Thermal Shock Resistance

23 points

Electrical

Electrical Conductivity: Equal Volume

7.2 % IACS

Electrical Conductivity: Equal Weight (Specific)

8.3 % IACS

Calculated

Resilience: Ultimate (Unit Rupture Work)

130 MJ/m 3

Resilience: Unit (Modulus of Resilience)

440 kJ/m 3

Stiffness to Weight: Axial

13 points

Stiffness to Weight: Bending

24 points

Strength to Weight: Axial

26 points

Strength to Weight: Bending

23 points

Environmental

Base Metal Price

2.1 % relative

Embodied Carbon

1.5 kg CO 2 /kg material

Embodied Energy

19 MJ/kg

Embodied Energy

19 MJ/kg 8.2 x 10 3 BTU/lb

Embodied Water

47 L/kg

Embodied Water

47 L/kg 5.6 gal/lb

Registered Designations & Aliases

1.12211.1221C60EC60EEN 1.1221 (C60E) Non-Alloy Steel

Standards

EN 10083-2 EN 10083-2: 2006 Steels for quenching and tempering. Technical delivery conditions for non alloy steels

EN 10132-3 EN 10132-3: 2000 Cold rolled narrow steel strip for heat treatment. Technical delivery conditions. Steels for quenching and tempering

EN 10250-2 EN 10250-2: 2000 Open steel die forgings for general engineering purposes. Non-alloy quality and special steels

EN 10250-2 EN 10250-2: Open die steel forgings for general engineering purposes - Part 2: Non-alloy quality and special steels

EN 10250-2 EN 10250-2: Open die steel forgings for general engineering purposes - Part 2: Non-alloy quality and special steels EN 10297-1: Seamless circular steel tubes for mechanical and general engineering purposes - Technical delivery conditions - Part 1: Non-alloy and alloy steel tubes

EN 10277-5 EN 10277-5: 2008 Bright steel products. Technical delivery conditions. Steels for quenching and tempering

EN 10297-1 EN 10297-1: 2003 Seamless circular steel tubes for mechanical and general engineering purposes. Non-alloy and alloy steel tubes. Technical delivery conditions

EN 10297-1 EN 10297-1: Seamless circular steel tubes for mechanical and general engineering purposes - Technical delivery conditions - Part 1: Non-alloy and alloy steel tubes