EN 1.0213 (C8C) Non-Alloy Steel
Carbon & Non-Alloy Steels
hot worked
Property Overview
Density7.9g/cm³
Elastic Modulus190GPa
Tensile Strength360MPa
Yield Strength220MPa
Brinell Hardness100HB
Maximum Service Temperature400°C
Chemical Composition
C
0.060 to 0.1%
MN
0.25 to 0.45%
SI
0 to 0.1%
P
0 to 0.020%
S
0 to 0.025%
AL
0.020 to 0.060%
FE
99.245 to 99.67%
Mechanical
Elastic (Young's, Tensile) Modulus
190 GPa
Elongation at Break
25 %
Fatigue Strength
160 MPa
Poisson's Ratio
0.29
Reduction in Area
74 %
Shear Modulus
73 GPa
Shear Strength
230 MPa
Tensile Strength: Ultimate (UTS)
360 MPa
Tensile Strength: Yield (Proof)
220 MPa
Hardness
Brinell Hardness
100
Physical
Density
7.9 g/cm 3
Thermal
Latent Heat of Fusion
250 J/g
Maximum Temperature: Mechanical
400 °C
Melting Completion (Liquidus)
1470 °C
Melting Onset (Solidus)
1430 °C
Specific Heat Capacity
470 J/kg-K
Thermal Conductivity
53 W/m-K
Thermal Diffusivity
14 mm 2 /s
Thermal Expansion
12 µm/m-K
Thermal Shock Resistance
11 points
Electrical
Electrical Conductivity: Equal Volume
6.9 % IACS
Electrical Conductivity: Equal Weight (Specific)
7.9 % IACS
Calculated
Resilience: Ultimate (Unit Rupture Work)
77 MJ/m 3
Resilience: Unit (Modulus of Resilience)
120 kJ/m 3
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
24 points
Strength to Weight: Axial
13 points
Strength to Weight: Bending
14 points
Environmental
Base Metal Price
1.8 % relative
Embodied Carbon
1.4 kg CO 2 /kg material
Embodied Energy
18 MJ/kg
Embodied Energy
18 MJ/kg 7.8 x 10 3 BTU/lb
Embodied Water
46 L/kg
Embodied Water
46 L/kg 5.5 gal/lb
Registered Designations & Aliases
1.02131.0213C8CC8CEN 1.0213 (C8C) Non-Alloy Steel
Standards
EN 10263-2 EN 10263-2: 2002 Steel rod, bars and wire for cold heading and cold extrusion.Technical delivery conditions for steels not intended for heat treatment after cold working
EN 10263-2 EN 10263-2: Steel rod, bars and wire for cold heading and cold extrusion - Part 2: Technical delivery conditions for steels not intended for heat treatment after cold working