5088 (5088-O, AlMg5Mn0.4) Aluminum
Wrought Aluminum Alloys
Property Overview
Density2.7g/cm³
Elastic Modulus68GPa
Tensile Strength310MPa
Yield Strength150MPa
Brinell HardnessUnknown
Maximum Service Temperature200°C
Chemical Composition
CR
0 to 0.15%
MN
0.2 to 0.5%
SI
0 to 0.2%
CU
0 to 0.25%
AL
92.4 to 94.8%
MG
4.7 to 5.5%
RES.
Residuals res. | | 0 to 0.15%
RESIDUALS RES.
0 to 0.15%
ZN
0.2 to 0.4%
ZR
0 to 0.15%
FE
0.1 to 0.35%
Mechanical
Elastic (Young's, Tensile) Modulus
68 GPa
Elongation at Break
29 %
Fatigue Strength
180 MPa
Poisson's Ratio
0.33
Shear Modulus
25 GPa
Shear Strength
200 MPa
Tensile Strength: Ultimate (UTS)
310 MPa
Tensile Strength: Yield (Proof)
150 MPa
Physical
Density
2.7 g/cm 3
Thermal
Latent Heat of Fusion
390 J/g
Maximum Temperature: Mechanical
200 °C
Melting Completion (Liquidus)
640 °C
Melting Onset (Solidus)
540 °C
Specific Heat Capacity
900 J/kg-K
Thermal Conductivity
120 W/m-K
Thermal Diffusivity
51 mm 2 /s
Thermal Expansion
24 µm/m-K
Thermal Shock Resistance
14 points
Electrical
Electrical Conductivity: Equal Volume
29 % IACS
Electrical Conductivity: Equal Weight (Specific)
98 % IACS
Calculated
Resilience: Ultimate (Unit Rupture Work)
76 MJ/m 3
Resilience: Unit (Modulus of Resilience)
170 kJ/m 3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
50 points
Strength to Weight: Axial
32 points
Strength to Weight: Bending
38 points
Environmental
Base Metal Price
9.5 % relative
Embodied Carbon
9.0 kg CO 2 /kg material
Embodied Energy
150 MJ/kg
Embodied Energy
150 MJ/kg 67 x 10 3 BTU/lb
Embodied Water
1180 L/kg
Embodied Water
1180 L/kg 140 gal/lb
Registered Designations & Aliases
5088 (5088-O, AlMg5Mn0.4) Aluminum5088-OA95088AlMg5Mn0.4EN AW-5088
Standards
EN 485-2 EN 485-2: Aluminium and aluminium alloys. Sheet, strip and plate. Mechanical properties
EN 485-2 EN 485-2: Aluminium and aluminium alloys. Sheet, strip and plate. Mechanical properties ISO 6361-2: Wrought aluminium and aluminium alloys - Sheets, strips and plates - Part 2: Mechanical properties EN 573-3: Aluminium and aluminium alloys. Chemical composition and form of wrought products. Chemical composition and form of products
EN 573-3 EN 573-3: Aluminium and aluminium alloys. Chemical composition and form of wrought products. Chemical composition and form of products
ISO 6361-2 ISO 6361-2: Wrought aluminium and aluminium alloys - Sheets, strips and plates - Part 2: Mechanical properties