UNS S30600 (310L NAG) Stainless Steel

Austenitic & General Stainless Steels

OverviewChemical CompositionMechanical PropertiesPhysical PropertiesOther Properties

Property Overview

Density7.6g/cm³
Elastic Modulus190GPa
Tensile Strength610MPa
Yield Strength270MPa
Brinell Hardness180HB
Maximum Service Temperature950°C
Weight Calculator

Chemical Composition

C
0 to 0.018%
CR
17 to 18.5%
NI
14 to 15.5%
MO
0 to 0.2%
MN
0 to 2.0%
SI
3.7 to 4.3%
P
0 to 0.020%
S
0 to 0.020%
CU
0 to 0.5%
FE
58.9 to 65.3%

Mechanical

Elastic (Young's, Tensile) Modulus
190 GPa
Elongation at Break
45 %
Fatigue Strength
250 MPa
Poisson's Ratio
0.28
Reduction in Area
56 %
Shear Modulus
76 GPa
Shear Strength
430 MPa
Tensile Strength: Ultimate (UTS)
610 MPa
Tensile Strength: Yield (Proof)
270 MPa

Hardness

Brinell Hardness
180

Physical

Density
7.6 g/cm 3

Thermal

Latent Heat of Fusion
350 J/g
Maximum Temperature: Corrosion
410 °C
Maximum Temperature: Mechanical
950 °C
Melting Completion (Liquidus)
1380 °C
Melting Onset (Solidus)
1330 °C
Specific Heat Capacity
490 J/kg-K
Thermal Conductivity
14 W/m-K
Thermal Diffusivity
3.7 mm 2 /s
Thermal Expansion
16 µm/m-K
Thermal Shock Resistance
14 points

Electrical

Electrical Conductivity: Equal Volume
2.1 % IACS
Electrical Conductivity: Equal Weight (Specific)
2.5 % IACS

Calculated

PREN (Pitting Resistance)
18
Resilience: Ultimate (Unit Rupture Work)
220 MJ/m 3
Resilience: Unit (Modulus of Resilience)
190 kJ/m 3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
25 points
Strength to Weight: Axial
22 points
Strength to Weight: Bending
21 points

Environmental

Base Metal Price
19 % relative
Embodied Carbon
3.6 kg CO 2 /kg material
Embodied Energy
51 MJ/kg
Embodied Energy
51 MJ/kg 22 x 10 3 BTU/lb
Embodied Water
150 L/kg
Embodied Water
150 L/kg 18 gal/lb
Registered Designations & Aliases
310L NAGS30600UNS S30600 (310L NAG) Stainless Steel
Standards

ASTM A182 ASTM A182: Standard Specification for Forged or Rolled Alloy and Stainless Steel Pipe Flanges, Forged Fittings, and Valves and Parts for High-Temperature Service

ASTM A240 ASTM A240: Standard Specification for Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip for Pressure Vessels and for General Applications

ASTM A479 ASTM A479: Standard Specification for Stainless Steel Bars and Shapes for Use in Boilers and Other Pressure Vessels

ASTM A479 ASTM A479: Standard Specification for Stainless Steel Bars and Shapes for Use in Boilers and Other Pressure Vessels ASTM A182: Standard Specification for Forged or Rolled Alloy and Stainless Steel Pipe Flanges, Forged Fittings, and Valves and Parts for High-Temperature Service ASTM A240: Standard Specification for Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip for Pressure Vessels and for General Applications Welding Metallurgy and Weldability of Stainless Steels, John C. Lippold and Damian J. Kotecki, 2005 ASTM A959: Standard Guide for Specifying Harmonized Standard Grade Compositions for Wrought Stainless Steels

ASTM A959 ASTM A959: Standard Guide for Specifying Harmonized Standard Grade Compositions for Wrought Stainless Steels