UNS S20433 Stainless Steel
Austenitic & General Stainless Steels
Property Overview
Density7.7g/cm³
Elastic Modulus200GPa
Tensile Strength630MPa
Yield Strength270MPa
Brinell Hardness190HB
Maximum Service Temperature900°C
Chemical Composition
C
0 to 0.080%
CR
17 to 18%
NI
3.5 to 5.5%
MN
5.5 to 7.5%
SI
0 to 1.0%
N
0.1 to 0.25%
P
0 to 0.045%
S
0 to 0.030%
CU
1.5 to 3.5%
FE
64.1 to 72.4%
Mechanical
Elastic (Young's, Tensile) Modulus
200 GPa
Elongation at Break
46 %
Fatigue Strength
250 MPa
Poisson's Ratio
0.28
Shear Modulus
76 GPa
Shear Strength
440 MPa
Tensile Strength: Ultimate (UTS)
630 MPa
Tensile Strength: Yield (Proof)
270 MPa
Hardness
Brinell Hardness
190
Rockwell B Hardness
82
Physical
Density
7.7 g/cm 3
Thermal
Latent Heat of Fusion
280 J/g
Maximum Temperature: Corrosion
410 °C
Maximum Temperature: Mechanical
900 °C
Melting Completion (Liquidus)
1400 °C
Melting Onset (Solidus)
1360 °C
Specific Heat Capacity
480 J/kg-K
Thermal Conductivity
15 W/m-K
Thermal Diffusivity
4.0 mm 2 /s
Thermal Expansion
17 µm/m-K
Thermal Shock Resistance
14 points
Electrical
Electrical Conductivity: Equal Volume
2.4 % IACS
Electrical Conductivity: Equal Weight (Specific)
2.8 % IACS
Calculated
PREN (Pitting Resistance)
20
Resilience: Ultimate (Unit Rupture Work)
230 MJ/m 3
Resilience: Unit (Modulus of Resilience)
180 kJ/m 3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
25 points
Strength to Weight: Axial
23 points
Strength to Weight: Bending
21 points
Environmental
Base Metal Price
13 % relative
Embodied Carbon
2.7 kg CO 2 /kg material
Embodied Energy
39 MJ/kg
Embodied Energy
39 MJ/kg 17 x 10 3 BTU/lb
Embodied Water
150 L/kg
Embodied Water
150 L/kg 18 gal/lb
Registered Designations & Aliases
S20433UNS S20433 Stainless Steel
Standards
ASTM A240 ASTM A240: Standard Specification for Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip for Pressure Vessels and for General Applications
ASTM A240 ASTM A240: Standard Specification for Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip for Pressure Vessels and for General Applications Welding Metallurgy of Stainless Steels, Erich Folkhard et al., 2012