EN 1.4962 (X12CrNiWTiB16-13) Stainless Steel
Other Steels
solution annealed (AT)
Property Overview
Density8.1g/cm³
Elastic Modulus200GPa
Tensile Strength630MPa
Yield Strength260MPa
Brinell Hardness190HB
Maximum Service Temperature910°C
Chemical Composition
C
0.070 to 0.15%
CR
15.5 to 17.5%
NI
12.5 to 14.5%
MN
0 to 1.5%
SI
0 to 0.5%
P
0 to 0.035%
S
0 to 0.015%
TI
0.4 to 0.7%
W
2.5 to 3.0%
B
0.0015 to 0.0060%
FE
62.1 to 69%
Mechanical
Elastic (Young's, Tensile) Modulus
200 GPa
Elongation at Break
34 %
Fatigue Strength
210 MPa
Poisson's Ratio
0.28
Shear Modulus
77 GPa
Shear Strength
420 MPa
Tensile Strength: Ultimate (UTS)
630 MPa
Tensile Strength: Yield (Proof)
260 MPa
Hardness
Brinell Hardness
190
Physical
Density
8.1 g/cm 3
Thermal
Latent Heat of Fusion
280 J/g
Maximum Temperature: Corrosion
510 °C
Maximum Temperature: Mechanical
910 °C
Melting Completion (Liquidus)
1480 °C
Melting Onset (Solidus)
1440 °C
Specific Heat Capacity
470 J/kg-K
Thermal Conductivity
14 W/m-K
Thermal Diffusivity
3.7 mm 2 /s
Thermal Expansion
16 µm/m-K
Thermal Shock Resistance
14 points
Electrical
Electrical Conductivity: Equal Volume
2.3 % IACS
Electrical Conductivity: Equal Weight (Specific)
2.6 % IACS
Calculated
PREN (Pitting Resistance)
21
Resilience: Ultimate (Unit Rupture Work)
170 MJ/m 3
Resilience: Unit (Modulus of Resilience)
170 kJ/m 3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
24 points
Strength to Weight: Axial
21 points
Strength to Weight: Bending
20 points
Environmental
Base Metal Price
23 % relative
Embodied Carbon
4.1 kg CO 2 /kg material
Embodied Energy
59 MJ/kg
Embodied Energy
59 MJ/kg 25 x 10 3 BTU/lb
Embodied Water
150 L/kg
Embodied Water
150 L/kg 17 gal/lb
Registered Designations & Aliases
1.49621.4962EN 1.4962 (X12CrNiWTiB16-13) Stainless SteelX12CrNiWTiB16-13X12CrNiWTiB16-13
Standards
EN 10088-1 EN 10088-1: 2005 Stainless steels. List of stainless steels
EN 10088-1 EN 10088-1: Stainless steels - Part 1: List of stainless steels
EN 10302 EN 10302: 2008 Creep resisting steels, nickel and cobalt alloys
EN 10302 EN 10302: Creep resisting steels, nickel and cobalt alloys
EN 10302 EN 10302: Creep resisting steels, nickel and cobalt alloys EN 10088-1: Stainless steels - Part 1: List of stainless steels Welding Metallurgy of Stainless Steels, Erich Folkhard et al., 2012