AISI 310H (S31009) Stainless Steel

Austenitic & General Stainless Steels

Overview Chemical Composition Mechanical Properties Physical Properties Other Properties

Property Overview

Density7.9g/cm³

Elastic Modulus200GPa

Tensile Strength580MPa

Yield Strength230MPa

Brinell Hardness190HB

Maximum Service Temperature1100°C

Weight Calculator

Chemical Composition

0.040 to 0.1%

24 to 26%

19 to 22%

0 to 2.0%

0 to 0.75%

0 to 0.045%

0 to 0.030%

49.1 to 57%

Mechanical

Elastic (Young's, Tensile) Modulus

200 GPa

Elongation at Break

40 %

Fatigue Strength

200 MPa

Poisson's Ratio

0.27

Reduction in Area

51 %

Shear Modulus

79 GPa

Shear Strength

400 MPa

Tensile Strength: Ultimate (UTS)

580 MPa

Tensile Strength: Yield (Proof)

230 MPa

Hardness

Brinell Hardness

190

Rockwell B Hardness

Physical

Density

7.9 g/cm 3

Thermal

Latent Heat of Fusion

300 J/g

Maximum Temperature: Corrosion

450 °C

Maximum Temperature: Mechanical

1100 °C

Melting Completion (Liquidus)

1410 °C

Melting Onset (Solidus)

1360 °C

Specific Heat Capacity

480 J/kg-K

Thermal Conductivity

15 W/m-K

Thermal Diffusivity

3.9 mm 2 /s

Thermal Expansion

16 µm/m-K

Thermal Shock Resistance

13 points

Electrical

Electrical Conductivity: Equal Volume

2.1 % IACS

Electrical Conductivity: Equal Weight (Specific)

2.4 % IACS

Calculated

PREN (Pitting Resistance)

Resilience: Ultimate (Unit Rupture Work)

190 MJ/m 3

Resilience: Unit (Modulus of Resilience)

130 kJ/m 3

Stiffness to Weight: Axial

14 points

Stiffness to Weight: Bending

25 points

Strength to Weight: Axial

21 points

Strength to Weight: Bending

20 points

Environmental

Base Metal Price

25 % relative

Embodied Carbon

4.3 kg CO 2 /kg material

Embodied Energy

61 MJ/kg

Embodied Energy

61 MJ/kg 26 x 10 3 BTU/lb

Embodied Water

190 L/kg

Embodied Water

190 L/kg 23 gal/lb

Registered Designations & Aliases

310HAISI 310HAISI 310H (S31009) Stainless SteelS31009

Standards

ASTM A182 ASTM A182: Standard Specification for Forged or Rolled Alloy and Stainless Steel Pipe Flanges, Forged Fittings, and Valves and Parts for High-Temperature Service

ASTM A240 ASTM A240: Standard Specification for Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip for Pressure Vessels and for General Applications

ASTM A479 ASTM A479: Standard Specification for Stainless Steel Bars and Shapes for Use in Boilers and Other Pressure Vessels

ASTM A479 ASTM A479: Standard Specification for Stainless Steel Bars and Shapes for Use in Boilers and Other Pressure Vessels Machining of Stainless Steels and Super Alloys: Traditional and Nontraditional Techniques, Helmi A. Youssef, 2016 ASTM A182: Standard Specification for Forged or Rolled Alloy and Stainless Steel Pipe Flanges, Forged Fittings, and Valves and Parts for High-Temperature Service ASTM A240: Standard Specification for Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip for Pressure Vessels and for General Applications ASTM A959: Standard Guide for Specifying Harmonized Standard Grade Compositions for Wrought Stainless Steels

ASTM A959 ASTM A959: Standard Guide for Specifying Harmonized Standard Grade Compositions for Wrought Stainless Steels