ASTM A369 Grade FP2 Cr-Mo Steel
Alloy Steels
Property Overview
Density7.9g/cm³
Elastic Modulus190GPa
Tensile Strength430MPa
Yield Strength240MPa
Brinell Hardness130HB
Maximum Service Temperature420°C
Chemical Composition
C
0.1 to 0.2%
CR
0.5 to 0.81%
MO
0.44 to 0.65%
MN
0.3 to 0.61%
SI
0.1 to 0.3%
P
0 to 0.025%
S
0 to 0.025%
FE
97.4 to 98.6%
Mechanical
Elastic (Young's, Tensile) Modulus
190 GPa
Elongation at Break
20 %
Fatigue Strength
160 MPa
Poisson's Ratio
0.29
Shear Modulus
73 GPa
Shear Strength
270 MPa
Tensile Strength: Ultimate (UTS)
430 MPa
Tensile Strength: Yield (Proof)
240 MPa
Hardness
Brinell Hardness
130
Physical
Density
7.9 g/cm 3
Thermal
Latent Heat of Fusion
250 J/g
Maximum Temperature: Mechanical
420 °C
Melting Completion (Liquidus)
1470 °C
Melting Onset (Solidus)
1430 °C
Specific Heat Capacity
470 J/kg-K
Thermal Conductivity
49 W/m-K
Thermal Diffusivity
13 mm 2 /s
Thermal Expansion
13 µm/m-K
Thermal Shock Resistance
13 points
Electrical
Electrical Conductivity: Equal Volume
7.2 % IACS
Electrical Conductivity: Equal Weight (Specific)
8.2 % IACS
Calculated
PREN (Pitting Resistance)
2.5
Resilience: Ultimate (Unit Rupture Work)
75 MJ/m 3
Resilience: Unit (Modulus of Resilience)
150 kJ/m 3
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
24 points
Strength to Weight: Axial
15 points
Strength to Weight: Bending
16 points
Environmental
Base Metal Price
2.6 % relative
Embodied Carbon
1.6 kg CO 2 /kg material
Embodied Energy
20 MJ/kg
Embodied Energy
20 MJ/kg 8.8 x 10 3 BTU/lb
Embodied Water
50 L/kg
Embodied Water
50 L/kg 6.0 gal/lb
Registered Designations & Aliases
ASTM A369 Grade FP2 Cr-Mo Steel
Standards
ASTM A369 ASTM A369: Standard Specification for Carbon and Ferritic Alloy Steel Forged and Bored Pipe for High-Temperature Service