ASTM A182 Grade F10 (S33100) Steel
Alloy Steels
Property Overview
Density7.9g/cm³
Elastic Modulus190GPa
Tensile Strength630MPa
Yield Strength230MPa
Brinell Hardness190HB
Maximum Service Temperature600°C
Chemical Composition
C
0.1 to 0.2%
CR
7.0 to 9.0%
NI
19 to 22%
MN
0.5 to 0.8%
SI
1.0 to 1.4%
P
0 to 0.040%
S
0 to 0.030%
FE
66.5 to 72.4%
Mechanical
Elastic (Young's, Tensile) Modulus
190 GPa
Elongation at Break
34 %
Fatigue Strength
180 MPa
Poisson's Ratio
0.29
Reduction in Area
56 %
Shear Modulus
74 GPa
Shear Strength
420 MPa
Tensile Strength: Ultimate (UTS)
630 MPa
Tensile Strength: Yield (Proof)
230 MPa
Hardness
Brinell Hardness
190
Physical
Density
7.9 g/cm 3
Thermal
Latent Heat of Fusion
290 J/g
Maximum Temperature: Mechanical
600 °C
Melting Completion (Liquidus)
1420 °C
Melting Onset (Solidus)
1370 °C
Specific Heat Capacity
470 J/kg-K
Thermal Expansion
13 µm/m-K
Thermal Shock Resistance
18 points
Electrical
Electrical Conductivity: Equal Volume
15 % IACS
Electrical Conductivity: Equal Weight (Specific)
17 % IACS
Calculated
PREN (Pitting Resistance)
8.0
Resilience: Ultimate (Unit Rupture Work)
170 MJ/m 3
Resilience: Unit (Modulus of Resilience)
140 kJ/m 3
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
24 points
Strength to Weight: Axial
22 points
Strength to Weight: Bending
21 points
Environmental
Base Metal Price
18 % relative
Embodied Carbon
3.6 kg CO 2 /kg material
Embodied Energy
51 MJ/kg
Embodied Energy
51 MJ/kg 22 x 10 3 BTU/lb
Embodied Water
120 L/kg
Embodied Water
120 L/kg 14 gal/lb
Registered Designations & Aliases
ASTM A182 Grade F10 (S33100) SteelS33100
Standards
ASTM A182 ASTM A182: Standard Specification for Forged or Rolled Alloy and Stainless Steel Pipe Flanges, Forged Fittings, and Valves and Parts for High-Temperature Service