EN 1.7216 (30CrMo4) Chromium-Molybdenum Steel
Other Steels
annealed
Property Overview
Density7.8g/cm³
Elastic Modulus190GPa
Tensile Strength650MPa
Yield Strength400MPa
Brinell Hardness200HB
Maximum Service Temperature420°C
Chemical Composition
C
0.27 to 0.34%
CR
0.8 to 1.2%
MO
0.15 to 0.3%
MN
0.35 to 0.6%
SI
0 to 0.35%
P
0 to 0.035%
S
0 to 0.035%
FE
97.2 to 98.4%
Mechanical
Elastic (Young's, Tensile) Modulus
190 GPa
Elongation at Break
23 %
Fatigue Strength
290 MPa
Poisson's Ratio
0.29
Shear Modulus
73 GPa
Shear Strength
410 MPa
Tensile Strength: Ultimate (UTS)
650 MPa
Tensile Strength: Yield (Proof)
400 MPa
Hardness
Brinell Hardness
200
Physical
Density
7.8 g/cm 3
Thermal
Latent Heat of Fusion
250 J/g
Maximum Temperature: Mechanical
420 °C
Melting Completion (Liquidus)
1460 °C
Melting Onset (Solidus)
1420 °C
Specific Heat Capacity
470 J/kg-K
Thermal Conductivity
46 W/m-K
Thermal Diffusivity
12 mm 2 /s
Thermal Expansion
13 µm/m-K
Thermal Shock Resistance
19 points
Electrical
Electrical Conductivity: Equal Volume
7.2 % IACS
Electrical Conductivity: Equal Weight (Specific)
8.3 % IACS
Calculated
Resilience: Ultimate (Unit Rupture Work)
130 MJ/m 3
Resilience: Unit (Modulus of Resilience)
430 kJ/m 3
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
24 points
Strength to Weight: Axial
23 points
Strength to Weight: Bending
21 points
Environmental
Base Metal Price
2.4 % relative
Embodied Carbon
1.5 kg CO 2 /kg material
Embodied Energy
20 MJ/kg
Embodied Energy
20 MJ/kg 8.5 x 10 3 BTU/lb
Embodied Water
50 L/kg
Embodied Water
50 L/kg 6.0 gal/lb
Registered Designations & Aliases
1.72161.721630CrMo430CrMo4EN 1.7216 (30CrMo4) Chromium-Molybdenum Steel
Standards
EN 10297-1 EN 10297-1: 2003 Seamless circular steel tubes for mechanical and general engineering purposes. Non-alloy and alloy steel tubes. Technical delivery conditions
EN 10297-1 EN 10297-1: Seamless circular steel tubes for mechanical and general engineering purposes - Technical delivery conditions - Part 1: Non-alloy and alloy steel tubes