2030 (AlCu4PbMg, A92030) Aluminum
Wrought Aluminum Alloys
T3
Property Overview
Density3.1g/cm³
Elastic Modulus70GPa
Tensile Strength390MPa
Yield Strength250MPa
Brinell HardnessUnknown
Maximum Service Temperature190°C
Chemical Composition
CR
0 to 0.1%
MN
0.2 to 1.0%
SI
0 to 0.8%
CU
3.3 to 4.5%
TI
0 to 0.2%
AL
88.9 to 95.2%
BI
0 to 0.2%
MG
0.5 to 1.3%
PB
0.8 to 1.5%
RES.
Residuals res. | | 0 to 0.3%
RESIDUALS RES.
0 to 0.3%
ZN
0 to 0.5%
FE
0 to 0.7%
Mechanical
Elastic (Young's, Tensile) Modulus
70 GPa
Elongation at Break
6.8 %
Fatigue Strength
91 MPa
Poisson's Ratio
0.33
Shear Modulus
26 GPa
Shear Strength
230 MPa
Tensile Strength: Ultimate (UTS)
390 MPa
Tensile Strength: Yield (Proof)
250 MPa
Physical
Density
3.1 g/cm 3
Thermal
Latent Heat of Fusion
390 J/g
Maximum Temperature: Mechanical
190 °C
Melting Completion (Liquidus)
640 °C
Melting Onset (Solidus)
510 °C
Specific Heat Capacity
870 J/kg-K
Thermal Conductivity
130 W/m-K
Thermal Diffusivity
50 mm 2 /s
Thermal Expansion
23 µm/m-K
Thermal Shock Resistance
17 points
Electrical
Electrical Conductivity: Equal Volume
34 % IACS
Electrical Conductivity: Equal Weight (Specific)
99 % IACS
Calculated
Resilience: Ultimate (Unit Rupture Work)
23 MJ/m 3
Resilience: Unit (Modulus of Resilience)
430 kJ/m 3
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
45 points
Strength to Weight: Axial
35 points
Strength to Weight: Bending
38 points
Environmental
Base Metal Price
10 % relative
Embodied Carbon
8.0 kg CO 2 /kg material
Embodied Energy
150 MJ/kg
Embodied Energy
150 MJ/kg 63 x 10 3 BTU/lb
Embodied Water
1140 L/kg
Embodied Water
1140 L/kg 140 gal/lb
Registered Designations & Aliases
2030 (AlCu4PbMg, A92030) AluminumA92030AlCu4PbMgEN AW-2030
Standards
EN 573-3 EN 573-3: Aluminium and aluminium alloys. Chemical composition and form of wrought products. Chemical composition and form of products
EN 754-2 EN 754-2: Aluminium and aluminium alloys. Cold drawn rod/bar and tube. Mechanical properties
EN 755-2 EN 755-2: Aluminium and aluminium alloys. Extruded rod/bar, tube and profiles. Mechanical properties