2011A (AlCu6BiPb(A)) Aluminum
Wrought Aluminum Alloys
T3
Property Overview
Density3.1g/cm³
Elastic Modulus70GPa
Tensile Strength320MPa
Yield Strength240MPa
Brinell HardnessUnknown
Maximum Service Temperature190°C
Chemical Composition
SI
0 to 0.4%
CU
4.5 to 6.0%
AL
91.5 to 95.1%
BI
0.2 to 0.6%
PB
0.2 to 0.6%
RES.
Residuals res. | | 0 to 0.15%
RESIDUALS RES.
0 to 0.15%
ZN
0 to 0.3%
FE
0 to 0.5%
Mechanical
Elastic (Young's, Tensile) Modulus
70 GPa
Elongation at Break
9.1 %
Fatigue Strength
92 MPa
Poisson's Ratio
0.33
Shear Modulus
26 GPa
Shear Strength
190 MPa
Tensile Strength: Ultimate (UTS)
320 MPa
Tensile Strength: Yield (Proof)
240 MPa
Physical
Density
3.1 g/cm 3
Thermal
Latent Heat of Fusion
390 J/g
Maximum Temperature: Mechanical
190 °C
Melting Completion (Liquidus)
660 °C
Melting Onset (Solidus)
550 °C
Specific Heat Capacity
870 J/kg-K
Thermal Conductivity
130 W/m-K
Thermal Diffusivity
49 mm 2 /s
Thermal Expansion
23 µm/m-K
Thermal Shock Resistance
14 points
Electrical
Electrical Conductivity: Equal Volume
33 % IACS
Electrical Conductivity: Equal Weight (Specific)
96 % IACS
Calculated
Resilience: Ultimate (Unit Rupture Work)
27 MJ/m 3
Resilience: Unit (Modulus of Resilience)
390 kJ/m 3
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
44 points
Strength to Weight: Axial
29 points
Strength to Weight: Bending
33 points
Environmental
Base Metal Price
11 % relative
Embodied Carbon
7.9 kg CO 2 /kg material
Embodied Energy
150 MJ/kg
Embodied Energy
150 MJ/kg 63 x 10 3 BTU/lb
Embodied Water
1150 L/kg
Embodied Water
1150 L/kg 140 gal/lb
Registered Designations & Aliases
2011A (AlCu6BiPb(A)) AluminumAlCu6BiPb(A
Standards
EN 573-3 EN 573-3: Aluminium and aluminium alloys. Chemical composition and form of wrought products. Chemical composition and form of products
EN 754-2 EN 754-2: Aluminium and aluminium alloys. Cold drawn rod/bar and tube. Mechanical properties
EN 754-2 EN 754-2: Aluminium and aluminium alloys. Cold drawn rod/bar and tube. Mechanical properties EN 755-2: Aluminium and aluminium alloys. Extruded rod/bar, tube and profiles. Mechanical properties
EN 755-2 EN 755-2: Aluminium and aluminium alloys. Extruded rod/bar, tube and profiles. Mechanical properties