2011 (AlCu6BiPb, 3.1655, FC1, A92011) Aluminum

Wrought Aluminum Alloys

Material conditionT3

Overview Chemical Composition Mechanical Properties Physical Properties Other Properties

Property Overview

Density3.1g/cm³

Elastic Modulus71GPa

Tensile Strength360MPa

Yield Strength280MPa

Brinell Hardness95HB

Maximum Service Temperature190°C

Weight Calculator

Chemical Composition

0 to 0.4%

5.0 to 6.0%

91.3 to 94.6%

0.2 to 0.6%

RES.

Residuals res. | | 0 to 0.15%

RESIDUALS RES.

0 to 0.15%

0 to 0.3%

0 to 0.7%

Mechanical

Elastic (Young's, Tensile) Modulus

71 GPa

Elongation at Break

12 %

Fatigue Strength

120 MPa

Poisson's Ratio

0.33

Shear Modulus

27 GPa

Shear Strength

220 MPa

Tensile Strength: Ultimate (UTS)

360 MPa

Tensile Strength: Yield (Proof)

280 MPa

Hardness

Brinell Hardness

Physical

Density

3.1 g/cm 3

Thermal

Latent Heat of Fusion

390 J/g

Maximum Temperature: Mechanical

190 °C

Melting Completion (Liquidus)

640 °C

Melting Onset (Solidus)

540 °C

Specific Heat Capacity

870 J/kg-K

Thermal Conductivity

150 W/m-K

Thermal Diffusivity

56 mm 2 /s

Thermal Expansion

23 µm/m-K

Thermal Shock Resistance

16 points

Electrical

Electrical Conductivity: Equal Volume

39 % IACS

Electrical Conductivity: Equal Weight (Specific)

110 % IACS

Calculated

Resilience: Ultimate (Unit Rupture Work)

39 MJ/m 3

Resilience: Unit (Modulus of Resilience)

540 kJ/m 3

Stiffness to Weight: Axial

13 points

Stiffness to Weight: Bending

44 points

Strength to Weight: Axial

32 points

Strength to Weight: Bending

36 points

Environmental

Base Metal Price

11 % relative

Embodied Carbon

7.9 kg CO 2 /kg material

Embodied Energy

150 MJ/kg

Embodied Energy

150 MJ/kg 63 x 10 3 BTU/lb

Embodied Water

1150 L/kg

Embodied Water

1150 L/kg 140 gal/lb

Registered Designations & Aliases

2011 (AlCu6BiPb, 3.1655, FC1, A92011) Aluminum3.1655A92011AlCu6BiPbEN AW-2011FC1

Standards

ASTM B210 ASTM B210: Standard Specification for Aluminum and Aluminum-Alloy Drawn Seamless Tubes

ASTM B210 ASTM B210: Standard Specification for Aluminum and Aluminum-Alloy Drawn Seamless Tubes ASTM B211: Standard Specification for Aluminum and Aluminum-Alloy Bar, Rod, and Wire EN 754-2: Aluminium and aluminium alloys. Cold drawn rod/bar and tube. Mechanical properties Aluminum: Properties and Physical Metallurgy, John E. Hatch (editor), 1984 EN 755-2: Aluminium and aluminium alloys. Extruded rod/bar, tube and profiles. Mechanical properties Aluminum Standards and Data, Aluminum Association Inc., 2013 EN 573-3: Aluminium and aluminium alloys. Chemical composition and form of wrought products. Chemical composition and form of products Properties and Selection: Nonferrous Alloys and Special-Purpose Materials, ASM Handbook vol. 2, ASM International, 1993

ASTM B211 ASTM B211: Standard Specification for Aluminum and Aluminum-Alloy Bar, Rod, and Wire

EN 573-3 EN 573-3: Aluminium and aluminium alloys. Chemical composition and form of wrought products. Chemical composition and form of products

EN 754-2 EN 754-2: Aluminium and aluminium alloys. Cold drawn rod/bar and tube. Mechanical properties

EN 755-2 EN 755-2: Aluminium and aluminium alloys. Extruded rod/bar, tube and profiles. Mechanical properties