1435 (A91435) Aluminum
Wrought Aluminum Alloys
annealed
Property Overview
Density2.7g/cm³
Elastic Modulus69GPa
Tensile Strength81MPa
Yield Strength23MPa
Brinell HardnessUnknown
Maximum Service Temperature170°C
Chemical Composition
MN
0 to 0.050%
SI
0 to 0.15%
CU
0 to 0.020%
TI
0 to 0.030%
AL
99.35 to 99.7%
MG
0 to 0.050%
ZN
0 to 0.1%
FE
0.3 to 0.5%
Mechanical
Elastic (Young's, Tensile) Modulus
69 GPa
Elongation at Break
32 %
Fatigue Strength
27 MPa
Poisson's Ratio
0.33
Shear Modulus
26 GPa
Shear Strength
54 MPa
Tensile Strength: Ultimate (UTS)
81 MPa
Tensile Strength: Yield (Proof)
23 MPa
Physical
Density
2.7 g/cm 3
Thermal
Latent Heat of Fusion
400 J/g
Maximum Temperature: Mechanical
170 °C
Melting Completion (Liquidus)
650 °C
Melting Onset (Solidus)
640 °C
Specific Heat Capacity
900 J/kg-K
Thermal Conductivity
230 W/m-K
Thermal Diffusivity
93 mm 2 /s
Thermal Expansion
23 µm/m-K
Thermal Shock Resistance
3.6 points
Electrical
Electrical Conductivity: Equal Volume
60 % IACS
Electrical Conductivity: Equal Weight (Specific)
200 % IACS
Calculated
Resilience: Ultimate (Unit Rupture Work)
20 MJ/m 3
Resilience: Unit (Modulus of Resilience)
3.8 kJ/m 3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
50 points
Strength to Weight: Axial
8.3 points
Strength to Weight: Bending
15 points
Environmental
Base Metal Price
9.0 % relative
Embodied Carbon
8.2 kg CO 2 /kg material
Embodied Energy
150 MJ/kg
Embodied Energy
150 MJ/kg 66 x 10 3 BTU/lb
Embodied Water
1190 L/kg
Embodied Water
1190 L/kg 140 gal/lb
Registered Designations & Aliases
1435 (A91435) AluminumA91435EN AW-1435
Standards
ASTM B483 ASTM B483: Standard Specification for Aluminum and Aluminum-Alloy Drawn Tube and Pipe for General Purpose Applications
ASTM B483 ASTM B483: Standard Specification for Aluminum and Aluminum-Alloy Drawn Tube and Pipe for General Purpose Applications Handbook of Aluminum vol. 2: Alloy Production and Materials Manufacturing, George Totten and D. Scott MacKenzie (editors), 2003 Aluminum: Properties and Physical Metallurgy, John E. Hatch (editor), 1984 Properties and Selection: Nonferrous Alloys and Special-Purpose Materials, ASM Handbook vol. 2, ASM International, 1993