AWS E410 (W41010) Weld Metal
Austenitic & General Stainless Steels
Property Overview
Density7.8g/cm³
Elastic Modulus190GPa
Tensile Strength580MPa
Yield Strength440MPa
Brinell HardnessUnknown
Maximum Service TemperatureUnknown
Chemical Composition
C
0 to 0.12%
CR
11 to 13.5%
NI
0 to 0.7%
MO
0 to 0.75%
MN
0 to 1.0%
SI
0 to 0.9%
P
0 to 0.040%
S
0 to 0.030%
CU
0 to 0.75%
FE
82.2 to 89%
Mechanical
Elastic (Young's, Tensile) Modulus
190 GPa
Elongation at Break
23 %
Poisson's Ratio
0.28
Shear Modulus
76 GPa
Tensile Strength: Ultimate (UTS)
580 MPa
Tensile Strength: Yield (Proof)
440 MPa
Physical
Density
7.8 g/cm 3
Thermal
Latent Heat of Fusion
270 J/g
Melting Completion (Liquidus)
1450 °C
Melting Onset (Solidus)
1400 °C
Specific Heat Capacity
480 J/kg-K
Thermal Conductivity
28 W/m-K
Thermal Diffusivity
7.5 mm 2 /s
Thermal Expansion
14 µm/m-K
Thermal Shock Resistance
16 points
Electrical
Electrical Conductivity: Equal Volume
2.9 % IACS
Electrical Conductivity: Equal Weight (Specific)
3.4 % IACS
Calculated
PREN (Pitting Resistance)
13
Resilience: Ultimate (Unit Rupture Work)
120 MJ/m 3
Resilience: Unit (Modulus of Resilience)
500 kJ/m 3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
25 points
Strength to Weight: Axial
21 points
Strength to Weight: Bending
20 points
Environmental
Base Metal Price
7.5 % relative
Embodied Carbon
2.0 kg CO 2 /kg material
Embodied Energy
28 MJ/kg
Embodied Energy
28 MJ/kg 12 x 10 3 BTU/lb
Embodied Water
100 L/kg
Embodied Water
100 L/kg 12 gal/lb
Registered Designations & Aliases
AWS E410 (W41010) Weld MetalW41010